Polyorganosiloxane hybrid pressure sensitive adhesive and methods for the preparation and use thereof

ABSTRACT

A polydiorganosiloxane having both a silicon bonded aliphatically unsaturated group and a silicon bonded poly(meth)acrylate polymer or copolymer is useful in a polyorganosiloxane hybrid pressure sensitive adhesive composition that cures to form a polyorganosiloxane hybrid pressure sensitive adhesive. The polyorganosiloxane hybrid pressure sensitive adhesive composition can be wet-cast or dry-cast on a substrate and cured to form a polyorganosiloxane hybrid pressure sensitive adhesive article. An adhesive article including the polyorganosiloxane hybrid pressure sensitive adhesive is also disclosed.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Patent Application No. 62/818,131 filed 14 Mar. 2019 under 35 U.S.C. § 119 (e). U.S. Provisional Patent Application No. 62/818,131 is hereby incorporated by reference.

TECHNICAL FIELD

A polyorganosiloxane having a silicon bonded poly(meth)acrylate group (hereinafter, “poly(meth)acrylate grafted polyorganosiloxane”) is useful in a hydrosilylation reaction curable polyorganosiloxane hybrid pressure sensitive adhesive (hybrid PSA) composition. Methods for making and using a hybrid PSA from the above mentioned composition are also disclosed.

BACKGROUND

Acrylic chains can be incorporated onto polydimethylsiloxane backbones using free-radical polymerization by performing the polymerization in the presence of mercapto-functional polydimethylsiloxanes. The mercapto group will act as a chain-transfer agent and enable acrylic chains to be grafted onto the polydimethylsiloxane chain as pendant and/or end groups. However, if a mercapto-functional polydimethylsiloxane also contained vinyl or other aliphatically unsaturated monovalent hydrocarbyl functionality, the system may become saturated or crosslinked due to reaction of the aliphatically unsaturated groups during the free radical polymerization. Furthermore, as chain-transfer is a kinetically controlled process, grafting efficiency may be low due to the low level of mercapto-functionalization.

SUMMARY

A polyorganosiloxane hybrid pressure sensitive adhesive composition comprises:

(I) a polyorganosiloxane having a poly(meth)acrylate group (hereinafter, “poly(meth)acrylate grafted polyorganosiloxane”), wherein the poly(meth)acrylate grafted polyorganosiloxane comprises unit formula: [R³ _(w)(R⁵—S—R″)(OR⁴)_((2-w))Si—O_(1/2)]_(p)[R³ _(v)(R⁵—S—R″)(OR⁴)_((1-v))Si—O_(2/2)]_(q)[(R⁵—S—R″)Si—O_(3/2)]_(k)(R⁶R⁷ ₂SiO_(1/2))_(r)(R⁷ ₂SiO_(2/2))_(s)(R⁶R⁷SiO_(2/2))_(t)(R⁷ ₃SiO_(1/2))_(u), where each subscript w is independently 0, 1, or 2, each subscript v is independently 0 or 1, each R³ is an independently selected monovalent hydrocarbon group; each R⁴ is an independently selected alkyl group; each R⁵ is an independently selected divalent hydrocarbon group, each R″ is independently a poly(meth)acrylate polymer or copolymer, each R⁶ is an independently selected aliphatically unsaturated monovalent hydrocarbon group, each R⁷ is an independently selected monovalent hydrocarbon group free of aliphatic unsaturation, subscript p≥0, subscript q≥0, subscript k≥0, a quantity (p+q+k)≥1, subscript r≥0, subscript s≥0, subscript t≥0, subscript u≥0, a quantity (r+t)≥2, and a quantity (p+q+k+r+s+t+u) is sufficient to provide a molecular weight of at least 50 kDa to the poly(meth)acrylate grafted polyorganosiloxane; (II) an organohydrogensilicon crosslinker having, per molecule, at least 3 silicon bonded hydrogen atoms; (III) a hydrosilylation reaction catalyst; optionally (IV) a hydrosilylation reaction inhibitor; (V) a polyorganosilicate resin; and optionally (XX) a solvent.

The hybrid PSA composition described above may be used to prepare an adhesive article in a method comprising:

1) coating the hybrid PSA composition on a surface of a substrate, and 2) curing the hybrid PSA composition to form a hybrid PSA on the surface of the substrate.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a representative example of Scheme 1 in which a (meth)acrylate polymer is grown off a thiol-functionality after a hydrogen atom is abstracted either from a free radical initiator fragment or a growing chain. The (meth)acrylate oligomer is then terminated/endcapped with a hydrogen atom from a different thiol molecule, thereby forming an alkoxysilyl-functional (meth)acrylate macromonomer. This is described below in Reference Example A.

FIG. 2 shows a representative example of Scheme 2 for making a poly(meth)acrylate grafted polyorganosiloxane described below in Reference Example B. In FIG. 2, a bis-vinyl-terminated polydimethylsiloxane, a bis-hydroxyl terminated polydimethylsiloxane, and the alkoxysilyl-functional (meth)acrylate macromonomer prepared in Scheme 1 in FIG. 1 are reacted in the presence of a phosphazene catalyst and solvent (toluene) to form a poly(meth)acrylate grafted polyorganosiloxane.

FIG. 3 shows Scheme 3 from Comparative Example 15, in which a bis-vinyl-terminated polydimethylsiloxane, a bis-silanol terminated polydimethylsiloxane, and mercapto-propylmethyldimethoxysilane are combined in the presence of phosphazene catalyst 1 and toluene, thereby making a mercapto-functionalized bis-vinyl terminated poly(dimethyl/methyl mercaptopropyl)siloxane copolymer.

FIG. 4 shows Scheme 4, in which a poly(dimethyl/methylvinyl)siloxane copolymer with polyacrylate endblocks is synthesized in Example 17.

FIG. 5 shows Scheme 5, in which a poly(dimethyl/methyl,vinyl/methyl,polyacrylate)siloxane copolymer with trimethylsiloxy endblocks is synthesized in Example 18.

DETAILED DESCRIPTION

A method is disclosed for making a product comprising a poly(meth)acrylate grafted polyorganosiloxane. The method comprises:

I) combining starting materials comprising:

-   -   A) an alkoxysilyl-functional (meth)acrylate macromonomer;     -   B) a polydiorganosiloxane selected from the group consisting of         -   B1) an unsaturated polydiorganosiloxane having, per             molecule, at least one silicon bonded aliphatically             unsaturated group;         -   B2) a hydroxyl-functional polydiorganosiloxane having, per             molecule, at least two silicon bonded hydroxyl groups, and         -   B3) a combination of B1) and B2);     -   C) a condensation reaction catalyst;     -   optionally D) a polydialkylsiloxane; and     -   optionally E) a solvent; thereby making the product comprising         the poly(meth)acrylate grafted polyorganosiloxane and a         by-product;

II) removing all or a portion of the by-product during and/or after step 1);

optionally III) neutralizing the product; and

optionally IV) recovering the poly(meth)acrylate grafted polyorganosiloxane.

Step I) in the method may be performed by any convenient means such as mixing. Step I) may be performed under inert conditions, e.g., nitrogen or other inert gas. Combining the starting materials may be performed at elevated temperature, e.g., heating at 80° C. to 120° C. Solvent may optionally be added, e.g., to facilitate combining the starting materials. Combining the starting materials may be performed with any order of addition, for example combining A) the alkoxysilyl-functional (meth)acrylate macromonomer, B) the polydiorganosiloxane (e.g., either or both of B1) the unsaturated polydiorganosiloxane, and B2) the hydroxyl-functional polydiorganosiloxane) and/or D) the polydialkylsiloxane. The resulting mixture may then be heated, and thereafter, C) the condensation reaction catalyst may be added, optionally dissolved in E) the solvent. Without wishing to be bound by theory, it is thought that adding E) the solvent may be beneficial to make a poly(meth)acrylate grafted polyorganosiloxane with high MW. When the starting materials react, a by-product is produced. The by-product may comprise water and/or alcohol (such as methanol). All or a portion of the by-product may be removed during and/or after step 1). Without wishing to be bound by theory, it is thought that removing by-product may drive the reaction to completion and/or facilitate increasing MW. By-product may be removed by any convenient means, such as stripping.

Step III) in the method is neutralizing the product. Neutralizing may be performed by adding F) a neutralizing agent to the product during or after step II). Neutralizing may be performed at ambient or elevated temperature. Step IV) in the method is recovering the poly(meth)acrylate grafted polyorganosiloxane. Recovering the poly(meth)acrylate grafted polyorganosiloxane may be performed by any convenient means, such as filtration, stripping, and/or distillation. The starting materials used in the method described above are as follows.

Starting material A), the alkoxysilyl-functional (meth)acrylate macromonomer used in the method described above may have formula A-1):

where each R³ is an independently selected monovalent hydrocarbon group; each R⁴ is an independently selected alkyl group; R⁵ is a divalent hydrocarbon group; R″ is a (meth)acrylate polymer or copolymer, and subscript a is 0, 1 or 2. R″ may have a DP of 1 to 1,000, and alternatively 5 to 600. Alternatively, the alkoxysilyl-functional (meth)acrylate macromonomer may have formula A-2):

where each R¹ is independently selected from the group consisting of hydrogen and an alkyl group; R² is independently selected from the group consisting of hydrogen, an alkyl group, an aryl group, and an aralkyl group; subscript n is 1 to 1,000; and R³, R⁴, and R⁵ are as described above.

Alternatively, in formula A-2), subscript n may be 5 to 600. Suitable alkyl groups for R¹ may be alkyl groups of 1 to 4 carbon atoms; alternatively methyl or ethyl. Alternatively, each R¹ may be methyl. Suitable alkyl groups for R² may have 1 to 18 carbon atoms, alternatively 1 to 8 carbon atoms. Suitable alkyl groups for R² include methyl, ethyl, propyl, and butyl. Suitable aryl groups for R² have 6 to 18 carbon atoms and include phenyl, and suitable aralkyl groups for R² have 6 to 18 carbon atoms and include styryl. Alternatively, in formula A-2) each R² may be an independently selected alkyl group of 1 to 18 carbon atoms, alternatively 1 to 8 carbon atoms.

Alternatively, in formulae A-1) and A-2), subscript a may be 1 or 2, alternatively 1, and alternatively 2. Each R³ may be an independently selected monovalent hydrocarbon group of 1 to 18 carbon atoms. Suitable monovalent hydrocarbon groups for R³ include alkyl groups (e.g., methyl, ethyl, propyl and butyl) and alkenyl groups (e.g., vinyl, allyl and hexenyl), aryl groups such as phenyl, and aralkyl groups such as benzyl, tolyl, xylyl, and phenylethyl. Alternatively, each R³ may be independently selected from the group consisting of alkyl and alkenyl. Alternatively, each R³ may be an alkyl group of 1 to 8 carbon atoms. Alternatively, each R³ may be selected from the group consisting of methyl and vinyl.

Each R⁴ may be an independently selected alkyl group of 1 to 6 carbon atoms. Suitable alkyl groups for R⁴ include methyl, ethyl, propyl, and butyl; alternatively methyl.

Each R⁵ may be a divalent hydrocarbon group of 1 to 18 carbon atoms. Suitable divalent hydrocarbon groups for R⁵ include alkylene groups such as ethylene (—CH₂—CH₂—), propylene such as —CH₂—CH₂—CH₂— or —CH(CH₃)CH₂—), butylene, or hexylene; an arylene group such as phenylene, or an alkarylene group such as:

Alternatively, R⁵ may be an alkylene group of 2 to 6 carbon atoms, such as propylene.

Starting material (A), the alkoxysilyl-functional (meth)acrylate macromonomer, may have a glass transition temperature (Tg) greater than −52° C. as calculated using the Fox equation.

$\frac{1}{T_{g,{Fox}}} = {\frac{w_{1}}{T_{g,1}} + \frac{w_{2}}{T_{g,2}}}$

Where T_(g,Fox) is the glass transition of the copolymer, T_(g,x) is the glass transition of the homopolymer x, and w_(x) is the weight fraction of x in the copolymer.

The amount of starting material A) used in the method for making the product comprising the poly(meth)acrylate grafted polyorganosiloxane described above depends on various factors, however, starting material A) may be used in an amount of 4% to 11% based on combined weights of starting materials A) and B) in the method. Alternatively, the amount of starting material A) may be 1% to 50%, alternatively 5% to 10%, alternatively 5% to 9%, on the same basis.

Alkoxysilyl-functional (meth)acrylate monomers suitable for use as starting material A) may be prepared by known methods, such as that disclosed in U.S. Pat. No. 6,733,884 to Brown. Alternatively, the alkoxysilyl-functional (meth)acrylate may be prepared by a method comprising:

1) combining starting materials comprising

-   -   i) a (meth)acrylate monomer of formula

where R¹ and R² are as described above;

-   -   ii) a mercapto-functional alkoxysilane of formula

where R³, R⁴, R⁵ and subscript a are as described above;

-   -   optionally iii) a free radical initiator; and     -   optionally iv) a solvent; thereby making a product comprising an         alkoxysilyl-functional (meth)acrylate macromonomer; and

optionally 2) recovering A) the alkoxysilyl-functional (meth)acrylate macromonomer.

In this method, i) the (meth)acrylate monomer may be combined with iv) the solvent, when present, before step 1). The solvent may optionally be dried before combining with starting material i) and/or any other starting materials. Alternatively, i) the (meth)acrylate monomer), ii) the mercapto-functional alkoxysilane, and iv) the solvent, when present, may be combined before step 1). The resulting combination may be heated, e.g., to 50° C. to 150° C. in a reactor. The reaction of starting materials i) and ii) may proceed with sufficient heating to generate free radicals. Alternatively, iii) the free radical initiator, optionally dissolved in iv) solvent, may be added to the reaction vessel. Step 1) may be performed under inert conditions, e.g., by purging the reactor with nitrogen. The starting materials in step 1) may be combined with mixing, heating, or both. For example, mixing and heating may be performed by mixing while heating from 50° C. to reflux temperature of the starting materials, alternatively 50° C. to 150° C., alternatively 50° C. to 110° C.; alternatively 50° C. to 100° C.; alternatively 75° C. to 85° C. for 1 to 6 hours. The starting materials may be added in any order, however, the iii) free radical initiator may be dissolved in iv) the solvent and optionally combined with i) the (meth)acrylate monomer, and the resulting combination may then be added into a reactor containing ii) the mercapto-functional alkoxysilane. Alternatively, i) the (meth)acrylate monomer and ii) the mercapto-functional alkoxysilane may be combined to form a mixture, and thereafter iii) the free radical initiator may be added to the mixture. Without wishing to be bound by theory, it is thought that the resulting alkoxysilyl-functional (meth)acrylate macromonomer (made with this order of addition) will have a different molecular weight distribution than when a different order of addition is used.

Step 2), recovering the alkoxysilyl-functional (meth)acrylate macromonomer may be performed by any convenient means, such as cooling the reaction product prepared in step 1) to RT, and precipitation in a non-solvent (such as an alkane such as hexanes or an alcohol such as methanol) which will precipitate the alkoxysilyl-functional (meth)acrylate macromonomer. Recovering may optionally further comprise drying the precipitate, such as by heating at ambient or reduced pressure with heat, e.g., from 80° C. to 100° C. to drive off residual monomer, solvent, or both.

In the method for preparing the alkoxysilyl-functional (meth)acrylate macromonomer starting material i) is a (meth)acrylate monomer. Suitable (meth)acrylate monomers have formula i-1):

where R¹ and R² are as described above. Suitable (meth)acrylate monomers are known in the art and are commercially available, and some examples are shown in Table 1. The amount of starting material i) may be 20% to 99.8%, alternatively 30% to 90%, and alternatively 70% to 75% based on combined weights of starting materials i), ii), iii), and iv).

TABLE 1 Exemplary (Meth)acrylate Monomers Abbrevia- (Meth) Acrylate T_(g), ° C. of Commercial tion Monomer homopolymer^(a) Source AA Acrylic Acid 101 Millipore Sigma BA Butyl Acrylate −53 Millipore Sigma BMA Butyl Methacrylate 20 Millipore Sigma 2-EHA 2-Ethylhexyl Acrylate −52 Millipore Sigma EHMA 2-Ethylhexyl 77 Millipore Sigma Methacrylate IBA Isobutyl Acrylate −33 Millipore Sigma IBMA Isobutyl Methacrylate 57 Millipore Sigma MMA Methyl Methacrylate 105 Millipore Sigma MAA Methacrylic Acid 228 Millipore Sigma BzMA benzyl methacrylate 55 Millipore Sigma PMA phenyl methacrylate 110 Millipore Sigma ^(a)Tg from Polymer Properties Database (polymerdatabase.com).

In the method for preparing the alkoxysilyl-functional (meth)acrylate macromonomer starting material ii) is a mercapto-functional alkoxysilane. The mercapto-functional alkoxysilane may have formula ii-1):

where subscript a and R³, R⁴, and R⁵ are as described above. Suitable mercapto-functional alkoxysilanes are known in the art and are commercially available. These include 3-mercaptopropyltrimethoxysilane, 3-mercaptopropyltriethoxysilane, 11-mercapto undecyltrimethoxysilane, (mercaptomethyl)methyldiethoxysilane, 3-mercaptopropylmethyldimethoxysilane are of which all commercially available from Gelest, Inc. of Morrisville, Pa., USA. Alternatively, mercapto-functional alkoxysilanes such as those described above as well as mercapto-functional monoalkoxysilanes, e.g., 3-mercaptopropyldimethylmethoxysilane and 3-mercaptopropyldimethylethoxysilane, may be synthesized by known methods such as those disclosed in U.S. Patent Application 2005/0124821 and Agina, E. V., ACS Applied Materials & Interfaces, 2015, 22, 11755-11764. The amount of starting material ii) may be 0.1% to 50%, alternatively 1% to 10%, and alternatively 1% to 8%, based on combined weights of starting materials i), ii), iii), and iv).

Starting material iii) for preparing the alkoxysilyl-functional (meth)acrylate macromonomer is a free radical initiator. The free radical initiator may be selected from the group consisting of iii-1) an azo compound, iii-2) a peroxide, (e.g., a hydroxyperoxide, a peracid, and a perester, such as a tert-alkyl peroxypivalate), and iii-3) a combination thereof. Suitable free radical initiators are known in the art, see for example, U.S. Pat. No. 8,258,243 col. 2, lines 9-34. Alternatively, suitable free radical initiators are commercially available. For example, tert-alkyl peroxypivalates are commercially available from Akzo Nobel, e.g., tert-amyl peroxypivalate is available as Trigonox 125-C75 and tert-butyl peroxypivalate is available as Trigonox 25-C75. The amount of starting material iii) may be 0 to 5%, alternatively 0.1% to 2%, and alternatively 1% to 2%, based on combined weights of starting materials i), ii), iii), and iv).

A solvent may be used in the method described above. One or more of the starting materials for use in making the alkoxysilyl-functional (meth)acrylate macromonomer may be dissolved in iv) a solvent before combining with the other starting materials. For example, the free radical initiator may be dissolved in mineral spirits. Alternatively, the solvent may be selected from the group consisting of iv-1) a hydrocarbon with a boiling point above 100° C. (e.g., an aromatic hydrocarbon such as toluene or xylene), iv-2) a polar solvent (such as acetone, methyl ethyl ketone, methyl acetate, ethyl acetate, acetonitrile, methanol, isopropanol or tert-butanol), iv-3) a silicone oil (e.g., the silicone oil may be a polydialkylsiloxane, as described below), and iv-4) a combination of two or more thereof. Alternatively, the solvent may be toluene, for example, to facilitate combination of starting material A) with the other starting materials to make the poly(meth)acrylate grafted polyorganosiloxane. When a polydialkylsiloxane is used as a solvent, the polydialkylsiloxane may act as a starting material in the method for making the product comprising the poly(meth)acrylate grafted polyorganosiloxane. When toluene is used, no solvent exchange may be included in the method for making the product comprising the poly(meth)acrylate grafted polyorganosiloxane. The amount of starting material iv) may be 0 to 70%, alternatively 0 to 25%, based on combined weights of starting materials i), ii), iii), and iv).

In the method for making the product comprising the poly(meth)acrylate grafted polyorganosiloxane, starting material B) is a polydiorganosiloxane. The polydiorganosiloxane is selected from the group consisting of B1) an unsaturated polydiorganosiloxane having, per molecule, at least one silicon bonded aliphatically unsaturated group, B2) a hydroxyl-functional polydiorganosiloxane having, per molecule, at least two silicon bonded hydroxyl groups, and B3) a combination of both B1) and B2). When the starting material B1) is used, the poly(meth)acrylate grafted polyorganosiloxane has both silicon bonded aliphatically unsaturated groups and silicon bonded poly(meth)acrylate groups.

Starting material B1) is an unsaturated polydiorganosiloxane having, per molecule, at least one silicon bonded aliphatically unsaturated group. The aliphatically unsaturated group may be in a terminal position, a pendant position, or both terminal and pendant positions.

Starting material B1), the unsaturated polydiorganosiloxane, may comprise unit formula B1-1): (R⁶R⁷ ₂SiO_(1/2))_(b)(R⁷ ₂SiO_(2/2))_(c)(R⁶R⁷SiO_(2/2))_(d)(R⁷ ₃SiO_(1/2))_(e)(R′OR⁷ ₂SiO_(1/2))_(f)(R′OR⁷SiO_(2/2))_(g), where each R⁶ is an independently selected aliphatically unsaturated hydrocarbon group, each R⁷ is an independently selected monovalent hydrocarbon group free of aliphatic unsaturation, each R′ is independently selected from the group consisting of H and R⁷, subscript b is 0, 1, or 2, subscript c≥1, subscript d≥0, subscript e is 0, 1, or 2, subscript f is 0, 1, or 2, and subscript g≥0, with the provisos that a quantity (b+d)≥1, a quantity (b+e+f)=2, and a quantity (b+c+d+e+f+g) is at least 3, alternatively 3 to 250.

Aliphatically unsaturated hydrocarbon groups for R⁶ may have 2 to 18 carbon atoms and are exemplified by alkenyl, such as vinyl, allyl or hexenyl; and alkynyl, such as propynyl, butynyl or hexynyl. Alternatively, each R⁶ may be an alkenyl group. Alternatively, each R⁶ may be a vinyl group.

Monovalent hydrocarbon groups free of aliphatic unsaturation for R⁷ may have 1 to 18 carbon atoms and are exemplified by alkyl groups, aryl groups, and aralkyl groups; alternatively alkyl groups and aryl groups. Suitable alkyl groups include methyl, ethyl, and propyl; alternatively methyl. Suitable aryl groups include phenyl. Alternatively, each R⁷ may be an alkyl group, such as methyl.

Alternatively, in unit formula B1-1), subscript b may be 0 or 2, subscript e may be 0 or 2, and subscript g may be 0. Alternatively, subscript c may be 1 to 250, subscript d may be 0 to 1, subscript g may be 0 to 1, and a quantity (c+d+g) may be 1 to 250. Alternatively, the quantity (b+e) may be 2. Alternatively, subscript c may be 1 to 100, alternatively 10 to 75, alternatively 25 to 75, and alternatively 30 to 60. Alternatively, subscript d may be 0 to 50, alternatively 0 to 25 alternatively 0 to 10, alternatively 0 to 5. Alternatively, subscript g may be 0 to 50, alternatively 0 to 25 alternatively 0 to 10, alternatively 0 to 5. Subscript b is 0 to 2, alternatively subscript b may be 0, and alternatively subscript b may be 2. Subscript e is 0 to 2, alternatively subscript e may be 0, and alternatively subscript e may be 2. Subscript f is 0 to 2, alternatively subscript f may be 0, and alternatively, subscript f may be 2.

Starting material B1) may contain both silicon bonded aliphatically unsaturated hydrocarbon groups and silicon bonded hydroxyl groups. Examples of starting material B1) containing both silicon bonded aliphatically unsaturated groups and silicon bonded hydroxyl groups include an OH-terminated polymethylvinylsiloxane and an OH-terminated poly(dimethyl/methylvinyl)siloxane copolymer, which is commercially available from Gelest. See for example, “Gelest Reactive Silicones: Forging New Polymer Links”, 2016, https://www.gelest.com/wp-content/uploads/Reactive-Silicones-No-Price-2016.pdf, at page 11. Alternatively, starting material B1) may have silicon bonded aliphatically unsaturated hydrocarbon groups, silicon bonded hydroxyl groups, and silicon bonded alkoxy groups. Examples of such material include DOWSIL™ 4-7042, which is a mixture of hydroxyl-terminated, poly(dimethyl, methylvinyl siloxane) and alpha-hydroxyl-terminated, omega-methoxy-terminated, poly(dimethyl, methylvinyl siloxane) commercially available from Dow Silicones Corporation of Midland, Mich., USA. When starting material B1) contains both silicon bonded aliphatically unsaturated hydrocarbon groups and sufficient silicon bonded hydroxyl groups, then starting material B2) the hydroxyl-functional polydiorganosiloxane is optional.

Alternatively, in unit formula B1-1) above, a quantity (f+g) may be less than 2 (such that starting material B1) may have less than 2 silicon bonded hydroxyl groups per molecule). Examples of suitable unsaturated polydiorganosiloxanes include

B-i) dimethylvinylsiloxy-terminated polydimethylsiloxane, B-ii) dimethylvinylsiloxy-terminated poly(dimethylsiloxane/methylvinylsiloxane), B-iii) dimethylvinylsiloxy-terminated polymethylvinylsiloxane, B-iv) trimethylsiloxy-terminated poly(dimethylsiloxane/methylvinylsiloxane), B-v) trimethylsiloxy-terminated polymethylvinylsiloxane, B-vi) dimethylvinylsiloxy-terminated poly(dimethylsiloxane/methylvinylsiloxane), B-vii) dimethylvinylsiloxy-terminated poly(dimethylsiloxane/methylphenylsiloxane), B-viii) dimethylvinylsiloxy-terminated poly(dimethylsiloxane/diphenylsiloxane), B-ix) phenyl,methyl,vinyl-siloxy-terminated polydimethylsiloxane, B-x) dimethylhexenylsiloxy-terminated polydimethylsiloxane, B-xi) dimethylhexenylsiloxy-terminated poly(dimethylsiloxane/methylhexenylsiloxane), B-xii) dimethylhexenylsiloxy-terminated polymethylhexenylsiloxane, B-xiii) trimethylsiloxy-terminated poly(dimethylsiloxane/methylhexenylsiloxane), B-xiv) trimethylsiloxy-terminated polymethylhexenylsiloxane B-xv) dimethylhexenyl-siloxy terminated poly(dimethylsiloxane/methylhexenylsiloxane), B-xvi) dimethylvinylsiloxy-terminated poly(dimethylsiloxane/methylhexenylsiloxane) B-xvii) a combination thereof. Vinyl functional polydiorganosiloxanes are available, see for example, “Gelest Reactive Silicones: Forging New Polymer Links”, 2016, https://www.gelest.com/wp-content/uploads/Reactive-Silicones-No-Price-2016.pdf, at pages 8-11 and 15-16. When starting material B1) does not contain sufficient silicon bonded hydroxyl groups, starting material B2) is used in the method described above. The amount of starting material B1) used in the method depends on various factors including on whether B1) has terminal, pendant, or both terminal and pendant aliphatically unsaturated groups, however, the amount of starting material B1) is sufficient to provide 0.1% to 10%, alternatively 0.1% to 2%, aliphatically unsaturated groups to all of the starting materials in step 1) of the method for making the product comprising the poly(meth)acrylate grafted polyorganosiloxane. Alternatively, the amount of starting material B1) may be 0.5% to 5%, alternatively, 1% to 4%, and alternatively 1% to 3%, based on combined weights of starting materials A) and B). Alternatively, starting material B1) can be present in a higher amount, e.g., up to 90% when B1) had hydroxyl functional groups and starting material B2) is not used.

In the method for making the product comprising the poly(meth)acrylate grafted polyorganosiloxane, starting material B2) is a hydroxyl-functional polydiorganosiloxane having, per molecule, at least two silicon bonded hydroxyl groups. The hydroxyl groups may be in terminal positions, in pendant positions, or both. Starting material B2) may comprise unit formula B2-1): (R⁸ ₂SiO_(2/2))_(h)(R⁸ ₃SiO_(1/2))_(i)(HOR⁸ ₂SiO_(1/2))_(j), where each R⁸ is an independently selected monovalent hydrocarbon group free of aliphatic unsaturation subscript j is 1 or 2, subscript i is 0 or 1, a quantity (j+i)=2, subscript h≥1, and a quantity (h+i+j) is at least 3, alternatively 3 to 250, and alternatively 3 to 100. Alternatively, subscript h may be 1 to 250, alternatively 1 to 100. Alternatively, i may be 0 and j may be 2. Monovalent hydrocarbon groups for R⁸ include alkyl groups, aryl groups, and aralkyl groups; alternatively alkyl groups and aryl groups. Suitable alkyl groups include methyl, ethyl, and propyl; alternatively methyl. Suitable aryl groups include phenyl. Alternatively, each R⁸ may be an alkyl group, such as methyl. Examples of starting material B2) include hydroxyl-terminated polydimethylsiloxane, hydroxyl-terminated poly(dimethyl/diphenyl)siloxane copolymers, hydroxyl-terminated poly(dimethyl/methylphenyl)siloxane copolymers. Alternatively, suitable bis-hydroxyl terminated polydimethylsiloxanes are commercially available from Dow Silicones Corporation of Midland, Mich., USA. Exemplary hydroxyl functional polydiorganosiloxanes are commercially available, which include the silanol functional polymers in “Gelest Reactive Silicones: Forging New Polymer Links”, 2016, https://www.gelest.com/wp-content/uploads/Reactive-Silicones-No-Price-2016.pdf, at pages 22 and 24-25. Starting material B2) may be used in an amount of 80% to 95%, alternatively 85% to 95% based on combined weights of starting materials A) and B); alternatively 87% to 94%, and alternatively 89% to 94%, on the same basis.

In the method for making the product comprising the poly(meth)acrylate grafted polyorganosiloxane, starting material C) is a phosphazene condensation reaction catalyst such as a phosphonitrile halide. Without wishing to be bound by theory, it is thought that cyclic siloxane by-products (such as octamethylcyclotetrasiloxane) formation may be minimized when the phosphazene condensation reaction catalyst is used in the method.

Phosphazene condensation reaction catalysts are exemplified by those disclosed in U.S. Pat. No. 9,051,428. Exemplary phosphazene condensation reaction catalysts may contain, per molecule at least one —(N=P<)— unit and may be an oligomer having up to 10 such phosphazene units, for example having an average of 1.5 to 5 phosphazene units. The phosphazene condensation reaction catalyst can for example be a halophosphazene, such as a chlorophosphazene (phosphonitrile chloride), an oxygen-containing halophosphazene, or an ionic derivative of a phosphazene such as a phosphazenium salt, such as an ionic derivative of a phosphonitrile halide, e.g., a perchlorooligophosphazenium salt.

One suitable type of phosphazene condensation reaction catalyst is an oxygen-containing halophosphazene, such as an oxygen-containing chlorophosphazene. Such an oxygen-containing chlorophosphazene can for example have the formula C-1):

In formula C-1) and C-2), subscript p can have an average value of 1 to 10, alternatively 1 to 5. The catalyst may also comprise tautomers of the catalyst of the formula C-2) Another type of suitable oxygen-containing chlorophosphazene has the formula C-3):

where R⁹ represents an organosilicon moiety bonded to phosphorus via oxygen, for example a phosphazene catalyst of the formula C-4):

where each R¹⁰ represents a monovalent hydrocarbon group having 1 to 18 carbon atoms or monovalent halogenated hydrocarbon group having 1 to 18 carbon atoms and subscript q has an average value of 1 to 10, alternatively 1 to 5. The catalyst may also comprise condensation products of such an organosilicon-containing phosphazene. All or some of the chlorine atoms in any of the above oxygen-containing phosphazenes can be replaced by radicals Q, in which Q represents a moiety selected from the group consisting of a hydroxyl group, a monovalent organic group, such as alkoxy or aryloxy, a halogen atom other than chlorine, an organosilicon group, and a phosphorus-containing group.

Another suitable type of phosphazene catalyst is a perchlorooligophosphazenium salt of the formula C-5):

where subscript o has an average value of 1 to 10, and Z⁻ represents an anion. Alternatively, subscript o may have an average value of 1 to 6, and alternatively, subscript o may have an average value of 2. The anion may be a complex anion and can, for example, be of the formula MX_((v+1)) in which M is an element having an electronegativity on Pauling's scale of from 1.0 to 2.0 and valency v, and X is a halogen atom. The element M can, for example, be phosphorus or antimony, alternatively phosphorus. The halogen atom for X may be Cl. The anion Z⁻ can alternatively be a complex anion of the formula [MX_((v−y+1))R¹¹ _(y)]⁻ where each R¹¹ is an independently selected alkyl group having 1 to 12 carbon atoms and subscript y has a value between 0 and v, as described in U.S. Pat. No. 5,457,220. Alternatively, in formula C-5), subscript o may have an average value of 2, and the anion Z⁻ may be PCl₆ ⁻.

The phosphazene condensation reaction catalyst may be present in an amount of 1 to 200, alternatively 2 to 200 parts per million based on the combined weight of starting materials A) and B), for example at 5 to 50 parts per million.

Starting material D) is an optional polydialkylsiloxane that may be added in step 1) of the method for making the product comprising the poly(meth)acrylate grafted polyorganosiloxane. The polydialkylsiloxane may comprise unit formula D-1): (R¹² ₂SiO_(2/2))_(m)(R¹² ₃SiO_(1/2))₂, where each R¹² is an independently selected alkyl group, and subscript m is 1 to 250, alternatively 1 to 50. Suitable alkyl groups for R¹² include methyl, ethyl, and propyl; alternatively methyl. Examples of starting material D) include Di) trimethylsiloxy-terminated polydimethylsiloxane, Dii) triethylsiloxy-terminated polydiethylsiloxane, and Diii) combinations of Di) and Dii). Polydialkylsiloxanes are known in the art and are commercially available. For example, methyl silicone fluids such as trimethylsiloxy-terminated polydimethylsiloxanes are commercially available from Gelest, see for example, “Gelest: Silicone Fluids,” https://www.gelest.com/themencode-pdf-viewer/?file=https://www.gelest.com:443/wp-content/uploads/Inert Silicones.pdf, 2012, at pages 8-9 and from Dow Silicones Corporation of Midland, Mich. USA under the tradename DOWSIL™ 200 Fluids. Trimethylsiloxy-terminated polydimethylsiloxane and triethylsiloxy-terminated polydiethylsiloxane are available from Power Chemical Corporation of Jiangsu, China. The amount of starting material D) depends on various factors including the molecular weight of the polydialkylsiloxane selected, however, when used, the amount may be 1% to 10% based on weights of starting materials A) to D) used in the method.

Starting material E) is a solvent that may be used in the method described above. The solvent may be an aromatic hydrocarbon such as toluene or xylene; or ethyl acetate. The amount and type of solvent are selected so as to solubilize both polyorganosiloxane and (meth)acrylate polymer or copolymer. However, when present, the solvent may be used in an amount of 30% to 80%, alternatively 40% to 70%, based on combined weights of starting materials A), B), C), D), and E).

Starting material F) is a neutralizing agent that may optionally be used in step III) of the method for making the product comprising the poly(meth)acrylate grafted polyorganosiloxane described above. Starting material F) may be used to neutralize the product after the poly(meth)acrylate grafted polyorganosiloxane forms. If a neutralizing agent is used, any neutralizing agent suitable for the catalyst chosen can be used, see for example the neutralizing agents disclosed in U.S. Pat. No. 8,580,862. Without wishing to be bound by theory, it is thought that selection of neutralizing agent depends on pKa and solubility. Suitable neutralizing agents for phosphazene-based condensation catalysts include, but are not limited to, alkylamines such as trioctylamine, trimethylamine, triethylamine, trihexylamine, and triisononylamine. Neutralizing agents are known in the art and are commercially available, e.g., from Millipore Sigma of St. Louis, Mo., USA. The amount of neutralizing agent depends on various factors including the amount of starting material C) the condensation catalyst, however, starting material F) may be present in an amount sufficient to provide a molar ratio of neutralizing agent to catalyst (F:C ratio) of 1:1 to 100:1, alternatively 1:1 to 30:1; and alternatively 1:1 to 20:1.

Starting Material (I) Poly(Meth)Acrylate Grafted Polyorganosiloxane

The method described above produces a poly(meth)acrylate grafted polyorganosiloxane. When starting material B-1) is used, the poly(meth)acrylate grafted polyorganosiloxane comprises unit formula: [R³ _(w)(R⁵—S—R″)(OR⁴)_((2-w))Si—O_(1/2)]_(p)[R³ _(v)(R⁵—S—R″)(OR⁴)_((1-v))Si—O_(2/2)]_(q)[(R⁵—S—R″)Si—O_(3/2)]_(k)(R⁶R⁷ ₂SiO_(1/2))_(r)(R⁷ ₂SiO_(2/2))_(s)(R⁶R⁷SiO_(2/2))_(t)(R⁷ ₃SiO_(1/2))_(u), where each subscript w is independently 0, 1, or 2, each subscript v is independently 0 or 1, each R³ is an independently selected monovalent hydrocarbon group; each R⁴ is an independently selected alkyl group; each R⁵ is an independently selected divalent hydrocarbon group, each R″ is independently a (meth)acrylate polymer or copolymer, each R⁶ is an independently selected aliphatically unsaturated monovalent hydrocarbon group, each R⁷ is an independently selected monovalent hydrocarbon group free of aliphatic unsaturation, subscript p≥0, subscript q≥0, subscript k≥0, a quantity (p+q+k)≥1, subscript r≥0, subscript s≥0, subscript t≥0, subscript u≥0, a quantity (r+t)≥2, and a quantity (p+q+k+r+s+t+u) is sufficient to provide a molecular weight of at least 50 kDa to the poly(meth)acrylate grafted polyorganosiloxane.

Alternatively, subscript w is 1 or 2. Alternatively, subscript p is 0 to 2, alternatively 1 or 2. Alternatively, subscript q is 0 to 100. Alternatively, subscript k<5; alternatively k may be 0, 1, or 2; and alternatively k=0. Alternatively, a quantity (p+q+k) is 1 to 100. Alternatively, subscript r is 0 to 2. Alternatively, subscript s is 0 to 100. Alternatively, subscript t is 0 to 100. Alternatively, subscript u is 0 to 2. Alternatively, the quantity (p+q+r+s+t+u) is sufficient to provide a molecular weight of 50 kDa to 1,000 kDa, alternatively 60 kDa to 1,000 kDa, alternatively 50 kDa to 600 kDa, and alternatively 60 kDa to 300 kDa, to the poly(meth)acrylate grafted polyorganosiloxane.

Alternatively, in the formula for the poly(meth)acrylate grafted polyorganosiloxane above, each R³ is an alkyl group of 1 to 6 carbon atoms. Alternatively, each R⁴ is an alkyl group of 1 to 6 carbon atoms. Alternatively, each R⁵ is an alkylene group of 2 to 8 carbon atoms. Alternatively, each R⁶ is an alkenyl group selected from vinyl, allyl and hexenyl. Alternatively, each R⁷ is an alkyl group of 1 to 6 carbon atoms.

The poly(meth)acrylate grafted polyorganosiloxane which has both a silicon bonded poly(meth)acrylate group and a silicon bonded aliphatically unsaturated group is useful in hydrosilylation reaction curable compositions. Without wishing to be bound by theory, it is thought that some or all of the silicon bonded aliphatically unsaturated group of the poly(meth)acrylate grafted polyorganosiloxane can react with silicon bonded hydrogen atoms. A hydrosilylation reaction curable composition comprises:

I) the poly(meth)acrylate grafted polyorganosiloxane having both a silicon bonded poly(meth)acrylate group and a silicon bonded aliphatically unsaturated group (as described above), II) an organohydrogensilicon crosslinker having, per molecule, at least 3 silicon bonded hydrogen atoms, and III) a hydrosilylation reaction catalyst. The hydrosilylation reaction curable composition may optionally further comprise one or more additional ingredients, such as IV) a hydrosilylation reaction catalyst inhibitor, V) a polyorganosilicate resin, VI) a spacer; VII) an extender, a plasticizer, or a combination thereof; VIII) a filler; IX) a filler treating agent; X) a biocide; XI) a flame retardant; XII) a surface modifier; XIII) a chain lengthener; XIV) an endblocker; XV) a flux agent; XVI) an anti-aging additive; XVII) a pigment; XVIII) an acid acceptor; XIX) a rheological additive; XX) a vehicle (e.g., a solvent or diluent); XXI) a surfactant; XXII) a corrosion inhibitor, and a combination thereof. Suitable organohydrogensilicon crosslinkers, hydrosilylation reaction catalysts, and additional starting materials are known in the art, for example, see U.S. Patent Application 2014/0228570, paragraphs [0096] to [0173] of which are hereby incorporated by reference.

In the hydrosilylation reaction composition, starting material II) is an organohydrogensilicon crosslinker, i.e., a compound having an average, per molecule, of 3 or more silicon bonded hydrogen atoms. Starting material II) may comprise a silane and/or a polyorganohydrogensiloxane compound. The amount of starting material II) in the composition depends on various factors including the SiH content of starting material II), the unsaturated group content of I) the poly(meth)acrylate grafted polyorganosiloxane, and the properties of the reaction product of the composition desired, however, the amount of starting material II) may be sufficient to provide a molar ratio of SiH groups in starting material II) to aliphatically unsaturated groups in starting material I) (commonly referred to as the SiH:Vi ratio) ranging from 0.3:1 to 40:1, alternatively 0.1:1 to 35:1, and alternatively 0.1:10 to 10:1. Starting material II) can have a linear, branched, cyclic, or resinous structure. When starting material II) is polymeric, then starting material II) can be a homopolymer or a copolymer. The silicon-bonded hydrogen atoms in starting material II) can be located at terminal, pendant, or at both terminal and pendant positions. Starting material II) may be one SiH functional compound. Alternatively, starting material II) may comprise a combination of two or more SiH functional compounds. Starting material II) may be two or more organohydrogenpolysiloxanes that differ in at least one of the following properties: structure, average molecular weight, viscosity, siloxane units, and sequence.

The organohydrogensilicon compound of starting material II) may comprise a polyorganohydrogensiloxane comprising siloxane units including, but not limited to, HR¹³ ₂SiO_(1/2), R¹³ ₃SiO_(1/2), HR¹³SiO_(2/2), R¹³ ₂SiO_(2/2), R¹³SiO_(3/2), HSiO_(3/2) and SiO_(4/2) units. In the preceding formulae, each R¹³ is an independently selected monovalent hydrocarbon groups. Suitable monovalent hydrocarbon groups for R¹³ include groups free of aliphatic unsaturation described above for R⁷.

Starting material II) may comprise a polyorganohydrogensiloxane of

R¹³ ₃SiO(R¹³ ₂SiO)_(aa)(R¹³HSiO)_(bb)SiR¹³ ₃,  Formula II-1):

R¹³ ₂HSiO(R¹³ ₂SiO)_(cc)(R¹³HSiO)_(dd)SiR¹³ ₂H, or  Formula II-2):

a combination thereof.

In formulae II-1) and II-2) above, subscript aa has an average value ranging from 0 to 2000, subscript bb has an average value ranging from 2 to 2000, subscript cc has an average value ranging from 0 to 2000, and subscript dd has an average value ranging from 0 to 2000. Each R¹³ is independently a monovalent hydrocarbon group, such as a monovalent hydrocarbon group free of aliphatic unsaturation, such as that described above for R⁷. R¹³ may have 1 to 18 carbon atoms. R¹³ may be alkyl or aryl. Suitable alkyl groups include methyl and ethyl, alternatively methyl. Suitable aryl groups include phenyl.

Polyorganohydrogensiloxanes for starting material II) are exemplified by:

a) dimethylhydrogensiloxy-terminated polydimethylsiloxane, b) dimethylhydrogensiloxy-terminated poly(dimethylsiloxane/methylhydrogensiloxane), c) dimethylhydrogensiloxy-terminated polymethylhydrogensiloxane, d) trimethylsiloxy-terminated poly(dimethylsiloxane/methylhydrogensiloxane), e) trimethylsiloxy-terminated polymethylhydrogensiloxane, f) a resin consisting essentially of H(CH₃)₂SiO_(1/2) units and SiO_(4/2) units, and g) a combination thereof.

Methods of making linear, branched, and cyclic organohydrogenpolysiloxanes suitable for use as starting material II), such as hydrolysis and condensation of organohalosilanes, are well known in the art. Methods of making organohydrogenpolysiloxane resins suitable for use as starting material II) are also well known as exemplified in U.S. Pat. Nos. 5,310,843; 4,370,358; and 4,707,531.

Such organohydrogensilicon compounds are commercially available and include, SYL-OFF™ SL2 CROSSLINKER and SYL-OFF™ SL12 CROSSLINKER, both of which are commercially available from Dow Silicones Corporation of Midland, Mich., U.S.A.

The exact amount of starting material II) in the composition depends on various factors including reactivity of I) the poly(meth)acrylate grafted polyorganosiloxane, the type and amount of starting material II), and the type and amount of any additional starting material (other than starting material II)), if present. However, the amount of starting material II) in the composition may range from >0% to 25%, alternatively 0.1% to 15%, and alternatively 1% to 5%, based on total weight of all starting materials in the composition.

Hydrosilylation reaction catalysts for starting material III) are known in the art and are commercially available. Hydrosilylation reaction catalysts include platinum group metal catalysts. Such hydrosilylation catalysts can be a metal selected from platinum, rhodium, ruthenium, palladium, osmium, and iridium. Alternatively, the hydrosilylation catalyst may be a compound of such a metal, for example, chloridotris(triphenylphosphane)rhodium(I) (Wilkinson's Catalyst), a rhodium diphosphine chelate such as [1,2-bis(diphenylphosphino)ethane]dichlorodirhodium or [1,2-bis(diethylphospino)ethane]dichlorodirhodium, chloroplatinic acid (Speier's Catalyst), chloroplatinic acid hexahydrate, platinum dichloride, and complexes of said compounds with low molecular weight organopolysiloxanes or platinum compounds microencapsulated in a matrix or coreshell type structure. Complexes of platinum with low molecular weight organopolysiloxanes include 1,3-diethenyl-1,1,3,3-tetramethyldisiloxane complexes with platinum (Karstedt's Catalyst). These complexes may be microencapsulated in a resin matrix. Alternatively, a hydrosilylation catalyst may comprise 1,3-diethenyl-1,1,3,3-tetramethyldisiloxane complex with platinum. Exemplary hydrosilylation catalysts are described in U.S. Pat. Nos. 3,159,601; 3,220,972; 3,296,291; 3,419,593; 3,516,946; 3,814,730; 3,989,668; 4,784,879; 5,036,117; and 5,175,325; and EP 0 347 895 B. Microencapsulated hydrosilylation catalysts and methods of making them are known in the art, as exemplified in U.S. Pat. Nos. 4,766,176 and 5,017,654.

The amount of catalyst used herein will depend on various factors including the selection of starting materials 1) and II) and their respective contents of silicon bonded hydrogen atoms and aliphatically unsaturated groups, and whether an inhibitor is present, however, the amount of catalyst is sufficient to catalyze hydrosilylation reaction of SiH and aliphatically unsaturated groups, alternatively the amount of catalyst is sufficient to provide 1 ppm to 1000 ppm of the platinum group metal based on combined weights of all starting materials, alternatively 5 ppm to 100 ppm, on the same basis.

Inhibitors for hydrosilylation reaction curable compositions for starting material IV are exemplified by acetylenic alcohols such as methyl butynol, ethynyl cyclohexanol, dimethyl hexynol, and 3,5-dimethyl-1-hexyn-3-ol, 1-butyn-3-ol, 1-propyn-3-ol, 2-methyl-3-butyn-2-ol, 3-methyl-1-butyn-3-ol, 3-methyl-1-pentyn-3-ol, 3-phenyl-1-butyn-3-ol, 4-ethyl-1-octyn-3-ol, 3,5-dimethyl-1-hexyn-3-ol, and 1-ethynyl-1-cyclohexanol, and a combination thereof; cycloalkenylsiloxanes such as methylvinylcyclosiloxanes exemplified by 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane, 1,3,5,7-tetramethyl-1,3,5,7-tetrahexenylcyclotetrasiloxane, and a combination thereof; ene-yne compounds such as 3-methyl-3-penten-1-yne, 3,5-dimethyl-3-hexen-1-yne; triazoles such as benzotriazole; phosphines; mercaptans; hydrazines; amines, such as tetramethyl ethylenediamine; fumarates such as dialkyl fumarates, dialkenyl fumarates, dialkoxyalkyl fumarates; maleates such as diallyl maleate; nitriles; ethers; carbon monoxide; alkenes such as cyclo-octadiene, divinyltetramethyldisiloxane; alcohols such as benzyl alcohol; and a combination thereof.

Alternatively, the inhibitor may be a silylated acetylenic compound. Without wishing to be bound by theory, it is thought that adding a silylated acetylenic compound reduces yellowing of the reaction product prepared from hydrosilylation reaction of the composition as compared to a reaction product from hydrosilylation of a composition that does not contain a silylated acetylenic compound or that contains an organic acetylenic alcohol stabilizer, such as those described above.

The silylated acetylenic compound is exemplified by (3-methyl-1-butyn-3-oxy)trimethylsilane, ((1,1-dimethyl-2-propynyl)oxy)trimethylsilane, bis(3-methyl-1-butyn-3-oxy)dimethylsilane, bis(3-methyl-1-butyn-3-oxy)silanemethylvinylsilane, bis((1,1-dimethyl-2-propynyl)oxy)dimethylsilane, methyl(tris(1,1-dimethyl-2-propynyloxy))silane, methyl(tris(3-methyl-1-butyn-3-oxy))silane, (3-methyl-1-butyn-3-oxy)dimethylphenylsilane, (3-methyl-1-butyn-3-oxy)dimethylhexenylsilane, (3-methyl-1-butyn-3-oxy)triethylsilane, bis(3-methyl-1-butyn-3-oxy)methyltrifluoropropylsilane, (3,5-dimethyl-1-hexyn-3-oxy)trimethylsilane, (3-phenyl-1-butyn-3-oxy)diphenylmethylsilane, (3-phenyl-1-butyn-3-oxy)dimethylphenylsilane, (3-phenyl-1-butyn-3-oxy)dimethylvinylsilane, (3-phenyl-1-butyn-3-oxy)dimethylhexenylsilane, (cyclohexyl-1-ethyn-1-oxy)dimethylhexenylsilane, (cyclohexyl-1-ethyn-1-oxy)dimethylvinylsilane, (cyclohexyl-1-ethyn-1-oxy)diphenylmethylsilane, (cyclohexyl-1-ethyn-1-oxy)trimethylsilane, and combinations thereof. Alternatively, the inhibitor is exemplified by methyl(tris(1,1-dimethyl-2-propynyloxy))silane, ((1,1-dimethyl-2-propynyl)oxy)trimethylsilane, or a combination thereof. The silylated acetylenic compound may be prepared by methods known in the art, such as silylating an acetylenic alcohol described above by reacting it with a chlorosilane in the presence of an acid receptor.

The amount of inhibitor added to the hydrosilylation reaction curable composition will depend on various factors including the desired pot life of the composition, whether the composition will be a one part composition or a multiple part composition, the particular inhibitor used. However, when present, the amount of inhibitor may range from 0% to 1%, alternatively 0% to 5%, alternatively 0.001% to 1%, alternatively 0.01% to 0.5%, and alternatively 0.0025% to 0.025%, based on the weight of all starting materials in the hydrosilylation reaction curable composition.

The hydrosilylation reaction curable composition may optionally further comprise starting material V) a polyorganosilicate resin. The polyorganosilicate resin is an MQ resin consisting essentially of R¹⁴ ₃SiO_(1/2) units and SiO_(4/2) units, where each R¹⁴ is independently selected from the group consisting of a hydroxyl group and a monovalent hydrocarbon group. The monovalent hydrocarbon group for R¹⁴ may be selected from the group consisting of an alkyl group of 1 to 18 carbon atoms, and an alkenyl group of 2 to 18 carbon atoms, and an aryl group or aralkyl group of 6 to 18 carbon atoms. Suitable alkyl groups, alkenyl groups, aryl groups, and aralkyl groups are as defined below. Alternatively each R¹⁴ may be a hydroxyl group or an alkyl group, such as methyl.

Alternatively, the polyorganosilicate resin may comprise unit formula (II): (R¹⁵ ₂R¹⁶SiO_(1/2))_(x)(R¹⁵ ₃SiO_(1/2))_(y)(SiO_(4/2))_(z), where R¹⁵ is an alkyl group, an aryl group, or an aralkyl group, such as methyl and phenyl; and R¹⁶ is an alkenyl group of 2 to 18 carbon atoms, such as vinyl, allyl or hexenyl; subscript x≥0, subscript y≥0, subscript z>0, a quantity (x+y)>0, and subscripts x, y, and z have values such that 0.9≤(x+y)/z≤1.3. Alternatively, the polyorganosilicate resin may comprise unit formula (III): (R¹⁵ ₃SiO_(1/2))_(w)(SiO_(4/2))_(z), where each R¹⁵ is as described above, subscript z is as described above, and subscript w>4.

The resin may contain an average of 0 to 30 mole percent of alkenyl groups, alternatively 3 to 30 mole percent of alkenyl groups, alternatively 0.1 to 30 mole percent, alternatively 0.1 to 5 mole percent, alternatively 3 to 10 mole percent. The mole percent of alkenyl groups in the resin is the ratio of the number of moles of alkenyl group-containing siloxane units in the resin to the total number of moles of siloxane units in the resin, multiplied by 100.

The Mn of the polyorganosilicate resin is typically greater than 3,000 Da, alternatively >3,000 Da to 8,000 Da, and alternatively 4,500 to 7,500 Da. Mn may be measured by GPC in the method described below.

Methods of making resins are well known in the art. For example, resin may be prepared by treating a resin copolymer produced by the silica hydrosol capping process of Daudt, et al. with at least an endblocking reagent such as hexamethyldisilazane or an alkenyl-containing endblocking agent. The method of Daudt et al., is disclosed in U.S. Pat. No. 2,676,182.

The method of Daudt, et al. involves reacting a silica hydrosol under acidic conditions with a hydrolyzable triorganosilane such as trimethylchlorosilane, a siloxane such as hexamethyldisiloxane, or mixtures thereof, and recovering a copolymer having M-units and Q-units. The resulting copolymers generally contain from 2 to 5 percent by weight of hydroxyl groups.

The resin, which typically contains less than 2% of silicon-bonded hydroxyl groups, may be prepared by reacting the product of Daudt, et al. with an endblocking agent such as an alkenyl group-containing endblocking agent and/or an endblocking agent free of aliphatic unsaturation, in an amount sufficient to provide from 0 to 30 mole percent of unsaturated organic groups in the final product. Examples of endblocking agents include, but are not limited to, silazanes, siloxanes, and silanes. Suitable endblocking agents are known in the art and exemplified in U.S. Pat. Nos. 4,584,355; 4,591,622; and 4,585,836. A single endblocking agent or a mixture of such agents may be used to prepare the resin.

Various suitable polyorganosilicate resins are commercially available from sources such as Dow Silicones Corporation of Midland, Mich., U.S.A., Momentive Performance Materials of Albany, N.Y., U.S.A., and Bluestar Silicones USA Corp. of East Brunswick, N.J., U.S.A. For example, DOWSIL™ MQ-1600 Solid Resin, DOWSIL™ MQ-1601 Solid Resin, and DOWSIL™ 1250 Surfactant, DOWSIL™ 7466 Resin, and DOWSIL™ 7366 Resin, all of which are commercially available from Dow Silicones Corporation of Midland, Mich., USA, are suitable for use herein. Such resins may be supplied in organic solvent.

A vehicle may optionally be used in the hydrosilylation reaction curable composition described herein. The vehicle may facilitate flow of the composition and introduction of certain ingredients, such as silicone resin. Vehicles used herein are those that help fluidize the ingredients of the composition but essentially do not react with the ingredients. The vehicle may be selected based on solubility of the ingredients in the composition and volatility. The solubility refers to the vehicle being sufficient to dissolve and/or disperse ingredients of the composition. Volatility refers to vapor pressure of the vehicle. If the vehicle is too volatile (having too high vapor pressure) bubbles may form in the composition during hydrosilylation reaction, and the bubbles may cause cracks or otherwise weaken or detrimentally affect properties of the reaction product. However, if the vehicle is not volatile enough (too low vapor pressure) the vehicle may remain as a plasticizer in the reaction product of the composition.

The vehicle may comprise an organic solvent. The organic solvent can be an alcohol such as methanol, ethanol, isopropanol, butanol, or n-propanol; a ketone such as acetone, methyl ethyl ketone, or methyl isobutyl ketone; an aromatic hydrocarbon such as benzene, toluene, or xylene; an aliphatic hydrocarbon such as heptane, hexane, or octane; a glycol ether such as propylene glycol methyl ether, dipropylene glycol methyl ether, propylene glycol n-butyl ether, propylene glycol n-propyl ether, or ethylene glycol n-butyl ether, a halogenated hydrocarbon such as dichloromethane, 1,1,1-trichloroethane or methylene chloride; chloroform; dimethyl sulfoxide; dimethyl formamide, acetonitrile; tetrahydrofuran; white spirits; mineral spirits; naphtha; n-methyl pyrrolidone; or a combination thereof.

Suitable vehicles include polyorganosiloxanes with suitable vapor pressures, such as hexamethyldisiloxane, octamethyltrisiloxane, hexamethylcyclotrisiloxane and other low molecular weight polyorganosiloxanes, such as 0.5 to 1.5 cSt DOWSIL™ 200 Fluids and DOWSIL™ OS FLUIDS, which are commercially available from Dow Silicones Corporation of Midland, Mich., U.S.A.

The amount of vehicle will depend on various factors including the type of vehicle selected and the amount and type of other starting materials selected. However, the amount of vehicle may range from 1% to 99%, alternatively 2% to 50%, based on the weight of all ingredients in the composition. The vehicle can be added during preparation of the composition, for example, to aid mixing and delivery of one or more starting materials. All or a portion of the vehicle may optionally be removed after the composition is prepared.

The hydrosilylation reaction curable composition may be a hybrid PSA composition. The hybrid PSA composition may comprise:

(I) a poly(meth)acrylate grafted polyorganosiloxane as described above for starting material (I), (II) an organohydrogensilicon crosslinker having, per molecule, at least 3 silicon bonded hydrogen atoms as described above for starting material (II); (III) a hydrosilylation reaction catalyst as described above for starting material (III) optionally (IV) a hydrosilylation reaction inhibitor as described above for starting material (IV); (V) a polyorganosilicate resin as described above for starting material (V); and optionally (XX) a solvent, as described above for the vehicle (XX).

The hybrid PSA composition may comprise 15% to 40%, alternatively 17% to 25% of poly(meth)acrylate grafted polyorganosiloxane. The hybrid PSA composition may comprise an amount of organohydrogensilicon crosslinker sufficient to provide an SiH content of starting material (II) to aliphatically unsaturated group (R⁶) content of starting material (I) (the SiH/Vi ratio) of 1:1 to 40:1, alternatively 10:1 to 35:1. The SiH:Vi ratio is a molar ratio. The hybrid PSA composition may comprise an amount of hydrosilylation reaction catalyst sufficient to provide 1 ppm to 150 ppm, alternatively 2 ppm to 50 ppm, of the platinum group metal to the hybrid PSA composition. When the hydrosilylation reaction inhibitor is present, the hybrid PSA composition may comprise an amount of the hydrosilylation reaction inhibitor sufficient to provide a weight ratio of starting material (III):starting material (IV) of up to 40:1. The hybrid PSA composition may comprise 5% to 60%, alternatively 25% to 40% of the polyorganosilicate resin. The hybrid PSA composition may comprise 0 to 70%, alternatively 40% to 60% of the solvent. All percentages are by weight based on combined weights of all starting materials in the hybrid PSA composition.

Method of Making the Hybrid PSA Composition

The hybrid PSA composition can be prepared by a method comprising combining all starting materials by any convenient means such as mixing at ambient or elevated temperature. The hydrosilylation reaction inhibitor may be added before the hydrosilylation reaction catalyst, for example, when the hybrid PSA composition will be prepared at elevated temperature and/or the hybrid PSA composition will be prepared as a one part composition.

The method may further comprise delivering one or more starting materials in a solvent (e.g., the polyorganosilicate resin and/or the hydrosilylation reaction catalyst) may be dissolved in a solvent when combined with one or more of the other starting materials in the hybrid PSA composition, and thereafter all or substantially all of the solvent may be removed by conventional means such as stripping and/or distillation, optionally with reduced pressure). One skilled in the art would understand that the resulting hybrid PSA composition contains no solvent or may contain trace amounts of residual solvent from delivery of a starting material, however, a solvent (e.g., organic solvent such as toluene or non-functional polydiorganosiloxane) is not intentionally added to the hybrid PSA composition.

Alternatively, the hybrid PSA composition may be prepared as a multiple part composition, for example, when the hybrid PSA composition will be stored for a long period of time before use, e.g., up to 6 hours before coating the hybrid PSA composition on a substrate. In the multiple part hybrid PSA composition, the hydrosilylation reaction catalyst is stored in a separate part from any starting material having a silicon bonded hydrogen atom, including the organohydrogensilicon crosslinker (II), and the parts are combined shortly before use of the hybrid PSA composition.

For example, a multiple part hybrid PSA composition may be prepared by combining starting materials comprising at least some of the poly(meth)acrylate grafted polyorganosiloxane, the organohydrogensilicon crosslinker, and optionally one or more other additional starting materials described above to form a base part, by any convenient means such as mixing. A curing agent may be prepared by combining starting materials comprising at least some of the poly(meth)acrylate grafted polyorganosiloxane, the hydrosilylation reaction catalyst, and optionally one or more other additional starting materials described above by any convenient means such as mixing. The starting materials may be combined at ambient or elevated temperature. The hydrosilylation reaction inhibitor may be included in one or more of the base part, the curing agent part, or a separate additional part. An optional anchorage additive may be added to the base part, or may be added as a separate additional part. The polyorganosilicate resin may be added to the base part, the curing agent part, or a separate additional part. An optional branched polyorganosiloxane may be added to the base part. When a two part hybrid PSA composition is used, the weight ratio of amounts of base part to curing agent part may range from 1:1 to 10:1. The hybrid PSA composition will cure via hydrosilylation reaction to form a hybrid PSA.

The method described above may further comprise one or more additional steps. The hybrid PSA composition prepared as described above may be used to form an adhesive article, e.g., a hybrid PSA (prepared by curing the hybrid PSA composition described above) on a substrate. The method may, therefore, further comprise applying the hybrid PSA composition to a substrate.

Applying the hybrid PSA composition to the substrate can be performed by any convenient means. For example, the hybrid PSA composition may be applied onto a substrate by gravure coater, comma coater, offset coater, offset-gravure coater, roller coater, reverse-roller coater, air-knife coater, or curtain coater.

The substrate can be any material that can withstand the curing conditions (described below) used to cure the hybrid PSA composition to form the pressure sensitive adhesive on the substrate. For example, any substrate that can withstand heat treatment at a temperature equal to or greater than 120° C., alternatively 150° C. is suitable. Examples of materials suitable for such substrates including plastic films such as polymethylmethacrylate (PMMA), polyimide (PI), polyetheretherketone (PEEK), polyethylene naphthalate (PEN), liquid-crystal polyarylate, polyamideimide (PAI), polyether sulfide (PES), polyethylene terephthalate (PET), polyethylene (PE), or polypropylene (PP). Alternatively, the substrate may be a plastic as described above coated on a paper backing. Alternatively, the substrate may be a metal foil such as aluminum foil or copper foil. The thickness of the substrate is not critical, however, the thickness may be 5 micrometers to 300 micrometers.

Alternatively, the substrate may be a fluorosilicone release liner, such as any one of the substrates described above coated with a fluorosilicone release coating.

To improve bonding of the hybrid PSA to the substrate, the method for forming the adhesive article may optionally further comprise treating the substrate before applying the hybrid PSA composition. Treating the substrate may be performed by any convenient means, such as applying a primer, or subjecting the substrate to corona-discharge treatment, etching, or plasma treatment before applying the hybrid PSA composition to the substrate.

An adhesive article such as a film or tape may be prepared by applying the hybrid PSA composition described above onto the substrate described above. When solvent is present, the method may optionally further comprise removing the all, or a portion, of the solvent before and/or during curing. Removing solvent may be performed by any convenient means, such as heating at a temperature that vaporizes the solvent without fully curing the hybrid PSA composition, e.g., heating at a temperature of 70° C. to 120° C., alternatively 50° C. to 100° C., and alternatively 70° C. to 80° C. for a time sufficient to remove all or a portion of the solvent (e.g., 30 seconds to 1 hour, alternatively 1 minute to 5 minutes).

Curing the hybrid PSA composition (and removing solvent, when solvent is present) may be performed by heating at a temperature of 80° C. to 200° C., alternatively 90° C. to 180° C., alternatively 100° C. to 160° C., and alternatively 110° C. to 150° C. for a time sufficient to cure the hybrid PSA composition (e.g., for 30 seconds to an hour, alternatively 1 to 5 minutes). If cure speed needs to be increased or the process oven temperatures lowered, the catalyst level can be increased. This forms a hybrid PSA on the substrate. Curing may be performed by placing the substrate in an oven. The amount of the hybrid PSA composition to be applied to the substrate depends on the specific application, however, the amount may be sufficient such that after curing thickness of the hybrid PSA may be 5 micrometers to 100 micrometers, and for protective film the thickness may be 6 micrometers to 50 micrometers, alternatively 8 micrometers to 40 micrometers, and alternatively 10 to 30 micrometers.

The method described herein may optionally further comprise applying a removable release liner to the hybrid PSA opposite the substrate, e.g., to protect the hybrid PSA before use of the adhesive article. The release liner may be applied before, during or after curing the hybrid PSA composition; alternatively after curing.

Alternatively, when the hybrid PSA is formed on the release liner, then the method further comprises applying a substrate (as described above) to the hybrid PSA after cure.

EXAMPLES

These examples are intended to illustrate the invention and should not be interpreted as limiting the scope set forth in the claims. Starting Materials used in the Examples are shown below in Table 2.

TABLE 2 Starting Materials Abbreviation Description Function Source BMA butyl methacrylate i) (meth)acrylate The Dow monomer Chemical Company MMA methyl methyacrylate i) (meth)acrylate The Dow monomer Chemical Company 2-EHA 2-ethylhexyl acrylate i) (meth)acrylate The Dow monomer Chemical Company AA Acrylic acid i) (meth)acrylate The Dow monomer Chemical Company BA Butyl acrylate i) (meth)acrylate The Dow monomer Chemical Company HSPrMeSi(OMe)₂ (3-mercaptopropyl)methyl, ii) alkoxysilane Millipore dimethoxysilane Sigma HSPrMe₂SiOMe (3-mercaptopropyl)dimethyl, ii) alkoxysilane Synthesized methoxysilane in Reference Example I, below tAPPiv tert-amyl peroxypivalate 75% iii) free radical initiator Akzo Nobel, solution in mineral spirits Trigonox 125-C75 tBPPiv tert-butyl peroxypivalate 75% iii) free radical initiator Akzo Nobel, solution in mineral spirits Trigonox 25- C75 EtOAc ethyl acetate iv) solvent Fisher Scientific OH terminated bis hydroxy terminated B2) hydroxyl Dow PDMS 1 polydimethylsiloxane with DP = 32 functional Silicones polydiorganosiloxane Corporation Vi-terminated bis vinyl terminated polydimethylsiloxane B1) unsaturated Dow PDMS 1 with DP = 48 polydiorganosiloxane Silicones Corporation Phosphazene Catalyst 1

C) condensation reaction catalyst Dow Silicones Corporation 4-7042 a mixture of hydroxy-terminated, B1) where B has both DOWSIL ™ poly(dimethyl, methylvinyl siloxane) and Vi and OH 4-7042 is alpha-hydroxy-terminated, omega- commercially methoxy-terminated, poly(dimethyl, available methylvinyl siloxane) from Dow Silicones Corporation MD₂₂M trimethyl-siloxy terminated D) polydialkylsiloxane Dow polydimethylsiloxane with DP = 22 Silicones Corporation Neutralizer trioctylamine F) neutralizing agent Millipore Sigma toluene toluene solvent Fisher Scientific heptanes heptanes solvent Fisher Scientific THF tetrahydrofuran solvent Fisher Scientific SiH crosslinker poly(dimethyl/methylhydrogen) II) organohydrogensilicon Dow siloxane copolymer crosslinker Silicones Corporation SiH crosslinker 2 trimethylsiloxy-terminated II) DOWSIL 6- poly(dimethyl/methylhydrogen) organohydrogensilicon 3570 from siloxane copolymer crosslinker Dow Silicones Corporation Karstedt's Catalyst III) hydrosilylation Dow reaction catalyst Silicones Corporation ETCH ethynyl cyclohexanol IV) hydrosilylation Millipore reaction inhibitor Sigma Resin 1 a polyorganosilicate resin having V) polyorganosilicate Dow (Me₃SiO_(1/2)) and (SiO_(4/2)) units, where Me resin Silicones represents a methyl group, with a Corporation molecular weight of 3800 Da to 4500 Da Resin 2 A solution of 74.7% of a polyorganosilicate V) polyorganosilicate Dow resin having (Me₃SiO_(1/2)) and (SiO_(4/2)) resin Silicones units, where Me represents a methyl group, Corporation with a molecular weight of 2900 Da by GPC; dissolved in balance of solvent

In this Reference Example A is provided a description of the process used to produce Macromonomer Example 1 (37 BMA/63 MMA, nomenclature refers to weight percent and BMA=butyl methacrylate and MMA=methyl methacrylate) with 1.9 weight percent (3-mercaptopropyl)methyldimethoxysilane based-on-monomer. The process was used to prepare the other alkoxysilyl-functional (meth)acrylate macromonomers in Examples MM-2 to MM-5 by varying appropriate starting materials and their amounts, as shown below in Table 3. Ethyl acetate (EtOAc) was dried over molecular sieves and other ingredients were used as supplied. A monomer mixture containing EtOAc (75 g), MMA (233 g), BMA (136.9 g) and (3-mercaptopropyl)methyldimethoxysilane (7 g) was prepared. EtOAc (100 g) and 12.5% of the monomer mixture (56.5 g) were added to a 4-neck 1-liter glass reactor equipped with a condenser and overhead mixer. The mixture was heated to 77° C. and sparged with nitrogen for 30 minutes. Trigonox 125-C75 (tAPPiv, 1 g) in EtOAc (10 g) was added to the reactor and held for 5 minutes. The temperature was slowly ramped to 85° C. and then the monomer mixture was fed at 0.1 mL/min for 180 min and an initiator solution (20 g of EtOAc; 2 g of Trigonox 125-C75) was fed over 240 min (180 min plus 60 min overfeed after monomer feed ends). The reaction was held at 85° C. for 180 min following the end of the initiator feed, and then the resulting mixture was allowed to cool to room temperature. The resulting mixture was precipitated in a large excess of hexanes three times and dried in a vacuum oven after each precipitation step. The final vacuum drying was done for at least 24 hrs and heated to 80-100° C. to drive off residual monomer and solvent. Example 4 deviated from this purification scheme because the BMA oligomers were soluble in hexanes so it was dried using a rotary evaporator. Table 3 summarizes the composition and characteristics of alkoxysilyl-functional (meth)acrylate macromonomers prepared using this method for each example.

In this Reference Example B is provided as a description of the process used to produce Macromonomer Example MM-6 (100 BMA) with 0.2 weight percent (3-mercaptopropyl)methyldimethoxysilane based-on-monomer. The process was used to prepare another alkoxysilyl-functional (meth)acrylate macromonomers (Example MM-7) by varying appropriate starting materials and their amounts, as shown below in Table 3. A monomer mixture of solvent (5 g), BMA (400 g) and (3-mercaptopropyl)methyldimethoxysilane (0.7 g) was prepared. Solvent (80 g) was added to a 4-neck 1 liter glass reactor equipped with a condenser and overhead mixer. The solvent was heated to 85° C. and then the monomer mixture (400.7 g) was fed over a period of 2 hours and the initiator solution was started 5 minutes later (20 g of solvent and 11 g of Trigonex 25-C75 tBPPiv) and was feed over a period of 4 hours. At 3 hours a BA (butyl acrylate, 4 g) shot was added. The reaction was held at 85° C. for 80 min following the end of the initiator feed, and then the mixture was allowed to cool to room temperature and collected. The reaction mixture was diluted with 50 g of toluene prior to collection.

In this Reference Example C is provided as a description of the process used to produce Example MM-8 (37 BMA/63 MMA) with 8.2 weight percent (3-mercaptopropyl)methyldimethoxysilane based-on-monomer. The process was used to prepare another alkoxysilyl-functional (meth)acrylate macromonomer (Example MM-9) by varying appropriate starting materials and their amounts, as shown below in Table 3. A monomer mixture of toluene (5 g), MMA (252 g), BMA (148 g) and (3-mercaptopropyl)methyldimethoxysilane (36 g) was prepared. Toluene (80 g) was added to a 4-neck 1 liter glass reactor equipped with a condenser and overhead mixer. The solvent was heated to 85° C. and then the monomer mixture (441 g) was fed over a period of 1 hour and the initiator solution (30 g of toluene and 16.5 g of Trigonex 25-C75 tBPPiv) was feed over a period of 3 hours. At 2 hours a BA (butyl acrylate, 10 g) chase was added over a period of 30 minutes. The reaction was held at 85° C. for 80 min following the end of the initiator feed, and then the mixture was allowed to cool to room temperature and collected. For X1, the reaction mixture was diluted with 160 g of toluene prior to collection, for X2 no additional dilution was required.

TABLE 3 Summary of alkoxysilyl-functional (meth)acrylate macromonomers Prepared in Reference Examples A-C Initiator CTA Macromonomer (mole % (moles % T_(g, Fox) Reference ID % BMA Initiator BOM*) BOM) (° C.) Example MM-1 37 tAppiv 0.3 1.2 68 A MM-2 37 tAppiv 0.3 7.6 68 A MM-3 100 tAppiv 0.4 1.5 20 A MM-4 100 tBPPiv 0.6 6.8 20 A MM-5 70 tBPPiv 0.5 2.2 41 A MM-6 100 tBPPiv 1.0 0.1 20 B MM-7 100 tBPPiv 1.7 28.0 20 B MM-8 37 tBPPiv 2.0 6.6 68 C MM-9 100 tBPPiv 2.8 7.1 20 C *BOM = based on monomers

The process used to produce Example MM-10 (90 BMA/10 AA) with 8.3 weight percent (3-mercaptopropyl)methyldimethoxysilane based-on-monomer. A monomer mixture of toluene (10 g), BMA (350 g) and (3-mercaptopropyl)methyldimethoxysilane (0.7 g) was prepared. Solvent (80 g) was added to a 4-neck 1 liter glass reactor equipped with a condenser and overhead mixer. The solvent was heated to 85° C. Once at temperature, as initial charge of BMA (10 g), AA (10 g) and (3-mercaptopropyl)methyldimethoxysilane (1.8 g) then the monomer mixture (384.2 g) was added to the reactor. After 5 minutes, the monomer mixture was fed over a period of 2 hours and the initiator solution (20 g of solvent and 11 g of Trigonex 25-C75 tBPPiv) and was fed over a period of 4 hours. The reaction was held at 85° C. for 80 min following the end of the initiator feed, and then the mixture was allowed to cool to room temperature and collected. The reaction mixture was diluted with 100 g of toluene prior to collection.

The process used to produce Example MM-11 (100 EHA) with 10.1 weight percent (3-mercaptopropyl)methyldimethoxysilane based-on-monomer. A monomer mixture of toluene (5 g), EHA (350) and (3-mercaptopropyl)methyldimethoxysilane (34.2 g) was prepared. Solvent (80 g) was added to a 4-neck 1 liter glass reactor equipped with a condenser and overhead mixer. The solvent was heated to 85° C. Once at temperature, as initial charge of EHA (20 g) and (3-mercaptopropyl)methyldimethoxysilane (1.8 g) then the monomer mixture (384.2 g) was added to the reactor. After 5 minutes, the monomer mixture was fed over a period of 2 hours and the initiator solution (20 g of solvent and 11 g of Trigonex 25-C75 tBPPiv) and was fed over a period of 4 hours. The reaction was held at 85° C. for 80 min following the end of the initiator feed, and then the mixture was allowed to cool to room temperature and collected.

The process used to produce Example MM-12 (90 EHA/10 AA) with 8.3 weight percent (3-mercaptopropyl)methyldimethoxysilane based-on-monomer. A monomer mixture of EHA (360 g), AA (40 g) and (3-mercaptopropyl)methyldimethoxysilane (36 g) was prepared. Solvent (80 g) was added to a 4-neck 1 liter glass reactor equipped with a condenser and overhead mixer. The solvent was heated to 85° C. Once at temperature, the monomer mixture was fed over a period of 2 hours and the initiator solution (20 g of solvent and 11 g of Trigonex 25-C75 tBPPiv) and was fed over a period of 4 hours. The reaction was held at 85° C. for 80 min following the end of the initiator feed, and then the mixture was allowed to cool to room temperature and collected.

TABLE 4 Summary of alkoxysilyl-functional (meth)acrylate macromonomers Examples MM-10 through MM-12 Monomer Initiator CTA Macromonomer Composition (mole % (moles % T_(g, Fox) ID (wt %) Initiator solvent BOM*) BOM) (° C.) MM-10 90% BMA/10% AA tBPPiv toluene 1.5 6.5 26 MM-11 100% EHA tBPPiv toluene 2.2 9.2 −52 MM-12  90% EHA/10% AA tBPPiv toluene 1.7 28 −43

TABLE 5 Characterization results of alkoxysilyl- functional (meth)acrylate macromonomers Example M_(n)/M_(w) ^(a) Residual Monomer % Silicone ID (kDa) PDI^(a) (ppm)^(b) condensed^(c) MM-1  7.7/15.1 2.0 75 MMA/341 BMA 0 MM-2 1.9/3.0 1.6 392 MMA/1880 BMA 9 MM-3  8.0/15.6 2.0 382 BMA 0 MM-4 3.2/4.8 1.5 139 MMA/5660 BMA 0 MM-5  7.9/12.0 1.5 751 BMA 0 MM-6 14/81 5.8 ND^(d) ND MM-7 0.62/6.5  10.5 ND ND MM-8 2.3/4.2 1.8 153 BMA & MMA ND MM-9 2.3/4.2 1.8 184 BMA ND MM-10 2.4/5.0 2.1 160 BMA/0 AA ND MM-11 1.9/3.2 1.7 501 EHA ND MM-12 2.4/4.5 1.9 130 EHA ND ^(a)Molecular weight distribution measured on a GPC using THF as the eluent. ^(b)Residual monomer concentration measured by HS-GC. A sample of the reaction mixture (~20 mg) was added to a vial in addition to an internal standard (~20 mg), and the vial was crimped. Head-space gas chromatography was performed by heating the vial and sampling the headspace to determine ppm levels of residual monomer. ^(c)Percent condensation of siloxane moieties measured by ²⁹Si NMR. ^(d)ND = not determined

In this Reference Example D, the alkoxysilyl-functional (meth)acrylate macromonomers of Examples MM-1 to MM-12 above were used to prepare poly(meth)acrylate grafted polyorganosiloxanes. The procedure was as follows: A 1-liter 4-neck round-bottom flask with a stirring rod and blade was pre-weighed and recorded prior to the start of the experiment. To this flask was added 181.0 grams OH terminated PDMS 1, 5.65 grams of Vi-terminated PDMS 1, 11.41 grams of the Example MM-5 (which had Mn=7.9 kDa and BMA=70%), and 238.5 grams of toluene were charged into the round-bottom flask equipped with an overhead mechanical stirrer, thermocouple, and a Dean Stark apparatus with a water-cooled condenser attached to a nitrogen bubbler. The heating mantle was plugged into a temperature controller to prevent the reaction mixture from heating to temperatures greater than 120° C. When the pot temperature reached 80° C., 0.47 mL of Phosphazene Catalyst 1 was added. As the reaction mixture continued to heat, the water, methanol, and toluene distillate was collected in a Dean Stark apparatus. Heating was discontinued after distilling enough toluene to obtain a final concentration of 60% solids solution, typically by removal of 100 g of distillate. Upon reaching the final concentration of 60% solids, 0.20 mL of trioctylamine was added to the reaction flask under stirring to neutralize the reaction mixture and the resulting mixture was allowed to cool to room temperature. After cooling to room temperature, the round-bottom flask with stirring rod and blade was weighed and recorded. The NVC was then calculated based on the mass balance (difference between pre-weight and final weight) assuming that all of the polymers content remained in the flask. Additionally, the vinyl content of the solution was calculated.

Example GP-2 to GP-20 were repeated using the procedure in Reference Example D, described above, except replacing the alkoxysilyl-functional (meth)acrylate macromonomers prepared in Example 5 with a different alkoxysilyl-functional (meth)acrylate macromonomer and changing the wt % of the alkoxysilyl-functional (meth)acrylate macromonomers. These examples are listed in Table 6.

TABLE 6 Summary of synthesized PDMS and selected properties. DSC Grafted Acrylic Si-Ac Curing Polysiloxane Macromonomer fraction Polymer peak ID ID (wt. %) Mw^(a) (kDa) PDI^(a) (° C.) Haze (%) Clarity (%) GP-1 MM-5 6 161 1.85 105.7 5.32 97.5 GP-2 MM-2 2 167 1.89 103.2 GP-3 MM-2 10 192 1.93 109.0 GP-4 MM-1 2 166 1.88 104.0 1.28 96.5 GP-5 MM-1 10 239 1.67 GP-6 MM-4 15 159 1.54 GP-7 MM-4 20 133 1.66 GP-8 MM-7 10 62 1.58 128.4 GP-9 MM-6 10 131 2.32 127.3 56.3 97.5 GP-10 MM-4 10 144 1.46 119.7 17.2 99.7 GP-11 MM-4 2 169 1.94 GP-12 MM-4 10 162 1.86 GP-13 MM-3 2 146 1.74 GP-14 MM-3 10 202 1.77 GP-15 MM-3 20 77 3.07 GP-16 MM-8 2 191 1.90 GP-17 MM-9 2 204 1.76 GP-18 MM-8 10 208 2.00 GP-19 MM-9 10 197 1.95 GP-20 MM-1 10 ND^(b) ND GP-21 MM-10 10 300 2.45 GP-22 MM-11 10 238 1.96 GP-23 MM-12 10 231 2.66 GP-24 NA 5.5 504 1.39 127.1 6.1 99.0 ^(a)MW and PDI determined by GPC analysis, ^(b)ND = Not determined *ultra high MW material might be present but was filtered out in GPC injection

In addition to the above polyacrylate grafted PDMS examples, several more examples with various structural variations are shown below.

Example GP-24—Synthesis of a poly(dimethyl,methylvinyl)siloxane Copolymer with Polyacrylate Ends

A monomer mixture of butylmethacrylate (200 g) and HSPrMe₂SiOMe (5 g) were added to a jar. An initiator solution was made of tBPPiv (5.5 g) and toluene (10 g). A four neck round bottom flask was charged with 40 grams of toluene. The toluene was heated to 8500, at which point the monomer and initiator mixtures were fed in over 2 and 4 hours, respectively. Butyl acrylate (2 g) was added to the flask 3 hours after the monomer mixture feed started. After the initiator feed ended, the reaction was maintained at 85° C. for 80 minutes. This produced an alkoxysilyl-functional (meth)acrylate macromonomer with 6.6 kDa 100 BMA.

A 1 L 4-neck round bottom flask with a stirring rod and blade was weighed before the experiment (571.50 g). In a typical synthesis shown in Scheme 4 in FIG. 4, 181.0 g of OH terminated PDMS 1, 2.46 g of 4-7042, 1.098 g of the above produced alkoxysilyl-functional (meth)acrylate macromonomer with 100 BMA, and 238 g of toluene were charged into the flask, which was equipped with a thermal couple and a Dean Stark apparatus with a water-cooled condenser adapted to nitrogen bubbler. The pot temperature was heated to 80-100° C. under nitrogen blanket, and 0.47 mL of Phosphazene Catalyst 1 was added. Then water, methanol, and toluene were collected in the Dean Stark apparatus when the pot temperature was raised to 103° C. Heating was stopped after distilling off a total of 67.0 g of distillates with pot temperature raised to 113° C. The reaction ran for 1 hour and 14 minutes from the time the catalyst was added at 80° C. until the quenching of the reaction. The reaction was stopped after only 67.0 grams of distillate due to viscosity of the polymer. Next 0.2 mL of trioctylamine (neutralizer) was added to the flask under stirring and the resulting mixture was allowed to cool to room temperature. After the pot temperature was cooled down to room temperature, the flask with stirring rod and blade was weighed again (930.0 g). The Non-volatile content (NVC) calculated based on the mass balance was 54.0% assuming that all of the polymers contents remained in the flask. The vinyl content of the resulting poly(meth)acrylate grafted polyorganosiloxane was 0.069%.

Example GP-25—Polyacrylate Grafted Pendant Vinyl PDMS with Methyl Ends

A 1 L 4-neck round bottom flask with a stirring rod and blade was weighed before the experiment (571.49 g). In a typical synthesis shown in Scheme 5 in FIG. 5, 181.0 g of OH terminated PDMS 1, 2.46 g of 4-7042, 2.70 g of MD₂₂M, 18.62 g of the alkoxysilyl-functional (meth)acrylate macromonomer prepared in Example 4, and 238 g of toluene were charged into the flask, which was also equipped with a thermal couple and a Dean Stark apparatus with a water-cooled condenser adapted to nitrogen bubbler. The pot temperature was heated to 80-100° C. under nitrogen blanket and 0.47 mL Phosphazene Catalyst 1 was added. Then water, methanol, and toluene were collected in the Dean Stark apparatus when the pot temperature was raised to 103° C. Heating was stopped after distilling off a total of 96.8 g of distillates with pot temperature raised to 113° C. The reaction ran for 1 hour and 20 minutes from the time the catalyst was added at 80° C. until the quenching of the reaction. Next 0.2 mL of trioctylamine (neutralizer) was added to the flask under stirring and the mixture was allowed to cool to room temperature. After the pot temperature was cooled down to room temperature, the flask with stirring rod and blade was weighed again (929.3 g). The Non-volatile content (NVC) calculated based on the mass balance was 57.2% assuming that all of the polymer contents remained in the flask. The sample was collected in a wide mouth bottle. The vinyl content of the resulting poly(meth)acrylate grafted polyorganosiloxane was 0.069%.

Example GP-26

In this Example GP-26, a bis-hydroxyl-terminated polydimethylsiloxane having pendant polybutylmethacrylate groups was synthesized as follows. A 1-liter 4-neck round-bottom flask with a stirring rod and blade was pre-weighed and recorded prior to the start of the experiment. To this flask was added 181.3 grams OH terminated PDMS 1, 18.17 grams of the macromonomer of Example MM-3 (which had Mn=8,000 g/mol and BMA=100%), and 239.61 grams of toluene were charged into the round-bottom flask equipped with an overhead mechanical stirrer, thermocouple, and a Dean Stark apparatus with a water-cooled condenser attached to a nitrogen bubbler. When the pot temperature reached 80-100° C. under nitrogen blanket, 0.47 mL of Phosphazene Catalyst 1 was added. As the reaction mixture continued to heat, the water, methanol, and toluene distillate was collected in a Dean Stark apparatus. Heating was discontinued after distilling enough toluene to obtain a final concentration of 50% solids solution. Upon reaching the final concentration of 50% solids, 0.20 mL of trioctylamine was added to the reaction flask under stirring to neutralize the reaction mixture and the resulting mixture was allowed to cool to room temperature. After cooling to room temperature, the round-bottom flask with stirring rod and blade was weighed and recorded. The NVC was then calculated based on the mass balance (difference between pre-weight and final weight) assuming that all of the polymers content remained in the flask.

Reference Example E—GPC Experimental Details

The molecular weight data was determined by analysis on a Waters 2695 model GPC. The poly(meth)acrylate grafted polyorganosiloxanes were dissolved in THE at a concentration of 5 mg solids/mL, and filtered through 0.45 μm PTFE syringe filters prior to injection of a 100 μL aliquot of the sample. The GPC was equipped with two Polymer Laboratories PLgel 5 μm Mixed-C columns (300 mm×7.5 mm), preceded by a PLgel 5 μm guard column (50 mm×7.5 mm) at a flow rate of 1.0 mL/min at 35° C. Detection was performed using a Waters 2410 differential refractive index detector. A conventional calibration of 16 narrow polystyrene standards covering the range of 580 g/mole to 2,300,000 g/mole and fit to a third order polynomial curve.

Reference Example F—General Procedure for Making and Curing Hydrosilylation Reaction Curable Compositions

Samples prepared in Examples GP-1 through GP-4 and GP-8 through GP-10 were mixed with SiH Crosslinker, Resin 1, Karstedt's catalyst, and ETCH based on a typical weight ratio of 44.1:2.7:53.2:0.4:0.05, and then 10 mg of the mixture was placed in a hermetic DSC pan and sealed. The sample weight was recorded. A TA instruments Q1 DSC method was run from RT to 200° C. at 10° C./min. An exothermal peak between 100 and 120° C. was typically observed for the hydrosilylation of the vinyl groups with silanes.

For the Benchmark, a vinyl terminated vinyl siloxane was prepared using 1-liter 4-neck round-bottom flask with a stirring rod and blade was pre-weighed and recorded prior to the start of the experiment. 169.4 grams OH terminated PDMS 1, 5.56 grams of Vi-terminated PDMS 1, and 219.5 grams of toluene were charged into the flask equipped with an overhead mechanical stirrer, thermocouple, and a Dean Stark apparatus with a water-cooled condenser attached to a nitrogen bubbler. The heating mantle was plugged into a temperature controller to prevent the reaction mixture from heating to temperatures greater than 120° C. When the pot temperature reached 84° C., 0.47 mL of Phosphazene Catalyst 1 was added. As the reaction mixture continued to heat, the water, methanol, and toluene distillate was collected in a Dean Stark apparatus. Heating was discontinued after distilling 96.1 g of azeotrope. Then 0.20 mL of trioctylamine was added to the reaction flask under stirring to neutralize the reaction mixture and the resulting mixture was allowed to cool to room temperature. The round-bottom flask with stirring rod and blade was weighed and recorded. The NVC was then calculated to be 59% based on the mass balance (difference between pre-weight and final weight) assuming that all of the polymers content remained in the flask. The MW of the resulting polymer was 153 kDa and the PDI was 1.98. The PSA was prepared according to the method outlined in Reference Example F.

Reference Example G—Film Sample Preparation

Create films: a sheet of paper was placed on a vacuum plate with vacuum on, then a sheet of release liner was placed on over the paper. The desired composition prepared as described above for Reference Example F was poured onto the release liner and a 4 mil bird bar was used to make a film. The film was placed in a Despatch™ oven at 150° C. for 5 minutes. After the sample was cooled a 2 inch×8½ strip was cut and transferred onto a glass substrate by using a ˜5 pound roller.

Reference Example H—Haze and Clarity

Optical properties (haze and clarity) were measured of a film sample prepared according to Reference Example F on a glass substrate with a haze-guard plus instrument from BYK Gardner.

Reference Example I—NMR

²⁹Si NMR spectra were acquired on an Agilent 500 MHz DD2 (mi-MR-06) system equipped with a 16 mm silicon free AutoX probe. The samples were prepared with CDCl₃+0.02M Cr(acac)₃ in a Si-free Teflon NMR tube. Standard parameters were applied except nt=1024. ¹H NMR spectra were acquired on a Bruker Avance III HD NMR spectrometer equipped with a 5 mm TCI H C/Si cryoprobe (mi-MR-07). The samples were prepared with CDCl₃ in a 5 mm NMR tube. Standard parameters were applied.

Reference Example J—Synthesis of HSPrMe2SiOMe

A 3 M solution of CH₃MgBr in diethyl ether (50 mL, 0.15 mol) was added dropwise to a solution of 3-mercaptopropyltrimethoxysilane (8.5 g, 0.043 mol) in 50 mL of THF, while the temperature was kept between 0 and 10° C. The reaction mixture was stirred for 1 h at 0° C. and then treated dropwise with CH₃OH (40 mL). The solid was filtered. The crude material was used directly into the next reaction. 5.4 g was collected to give a 75% yield of pure product. NMR is consistent with the literature reference, Agina, E. V., ACS Applied Materials & Interfaces, 2015, 22, 11755-11764.

Reference Example K—Hybrid PSA Composition

A general procedure for preparing a hybrid PSA composition was as follows (Examples PSA-1 through PSA-11): 70.62 grams of a solution including 61% of a polyorganosiloxane listed in Table 7 having both aliphatically unsaturated groups and poly(meth)acrylate groups prepared as described (balance was a solvent), 36.39 grams of xylene, 90.76 grams of Resin 2 (described above), 2.12 g SiH crosslinker 2 (described above), and 0.11 g of ETCH were added to a glass jar and blended together. 88.5 weight parts of the resulting base were mixed with 11.5 parts of toluene and 0.4 parts Karstedt's catalyst and mixed until homogenous. The resulting hybrid PSA composition was coated on a 2 mil thick sheet of polyester, and a 2 mil thick sheet of polyester coated with fluoro-release coating, using a 4 mil coating bar. Each sheet was then cured at 150° C. for 5 minutes,

Reference Example L—Peel Adhesion (PMMA)

Peel adhesion (180°) was tested according to PSTC-101 standards. A TMI Release and Adhesion Tester was used to pull a 1 inch wide strip of hybrid PSA coated onto 2 mil polyester film prepared as described in Reference Example K from a clean PMMA panel at 12 inches per minute. Results were reported in grams/inch. A sample passed if it showed adhesive failure/clean removal of the strip from the PMMA panel.

Reference Example M—Tack

Tack was tested according to ASTM D-2979. A PT-1000 Probe Tack Tester was used to obtain tack measurements from hybrid PSA samples coated onto 2 mil polyester film prepared as described in Reference Example K. Dwell time was set to 1.0 sec. Results were reported in grams.

Reference Example N—Release Force

Hybrid PSA composition samples prepared as described in Example 19 were applied to a fluoro-release coating using the wet-cast technique. Release was measured using a TMI Release and Adhesion Tester by pulling the fluoro-release liner side of the laminate from the polyester film side of a 1 inch wide strip of laminate (fluoro-release liner/adhesive/2 mil polyester film) at 12 inches per minute.

The data in Table 7 demonstrates a range of adhesion, tack and release forces. Without wishing to be bound by theory, it is thought that the macromonomer composition and loading enables property adjustment in otherwise similar hybrid PSA formulations.

TABLE 7 Summary of PSA formulations from Reference Example L and related properties (Reference Examples L-N). PMMA Release Grafted Adhesion Tack Force PSA ID Polysiloxane (g/in) (grams) (g/in) Benchmark NA 924 918 227 PSA-1 GP-4 1187 1067 252 PSA-2 GP-20 1023 1248 96 PSA-3 GP-13 1049 1038 235 PSA-4 GP-14 1173 1195 161 PSA-5 GP-15 1341 1195 22 PSA-6 GP-1 959 1049 180 PSA-7 GP-16 1073 1092 262 PSA-8 GP-17 957 1017 302 PSA-9 GP-21 701 887 74 PSA-10 GP-22 774 773 326 PSA-11 GP-23 516 677 71

INDUSTRIAL APPLICABILITY

There is an industry need to incorporate (meth)acrylic polymers and copolymers into polydiorganosiloxane (such as polydimethylsiloxanes) to increase interactions with substrate surfaces while retaining vinyl or other aliphatically unsaturated reactive functionality on the polydiorganosiloxanes that would be destroyed via free radical polymerization of an acrylic polymer onto the polydiorganosiloxane. The aliphatically unsaturated functionality will then be available for subsequent reactions (e.g., hydrosilylation cure). The hydrosilylation reaction curable composition, described above, may be useful as a polyorganosiloxane hybrid pressure sensitive adhesive composition.

The polyorganosiloxane hybrid pressure sensitive adhesive composition cures to form a polyorganosiloxane hybrid pressure sensitive adhesive. The polyorganosiloxane hybrid pressure sensitive adhesive composition can be wet-cast or dry-cast on a substrate and cured to form an adhesive article. As shown by the examples above, the adhesive article including the polyorganosiloxane hybrid pressure sensitive adhesive has good tack, good peel adhesion and good release force from polymeric substrates, regardless of the casting method selected.

The polyorganosiloxane hybrid pressure sensitive adhesive (hybrid PSA) and/or the adhesive article including the hybrid PSA can be used in various applications, including plasma tape, electrical tape, transdermal drug delivery, automotive display, electronic display, splicing tape, electronic assembly, labels. For example, the hybrid PSA may be used in addition to, or instead of, the pressure sensitive adhesives in U.S. Patent Application Publication 20120095159 or PCT Publication WO2007145996 or PCT Publication WO2008081913.

Definitions and Usage of Terms

Table 7 shows the abbreviations used herein.

TABLE 7 Abbreviations Abbreviation Definition AA Acrylic acid BMA Butyl methacrylate Da Daltons DSC differential scanning calorimetry 2-EHA or EHA 2-ethyl hexyl acrylate g grams HS-GC Headspace gas chromatography measured as described above GPC gel permeation chromatography KDa kilo Daltons L liters mg milligrams MHz megaHertz min minutes mL milliliters mm millimeters MMA Methyl methacrylate mmole millimoles Mn number average molecular weight determined by GPC Mw weight average molecular weight determined by GPC MW Molecular weight NMR nuclear magnetic resonance NVC non-volatile content PDI polydispersity determined by GPC PDMS polydimethylsiloxane ppm parts per million, by weight RT room temperature of 20° C. to 25° C. μm micrometer

All amounts, ratios, and percentages are by weight unless otherwise indicated. The articles ‘a’, ‘an’, and ‘the’ each refer to one or more, unless otherwise indicated by the context of the specification. The disclosure of ranges includes the range itself and also anything subsumed therein, as well as endpoints. For example, disclosure of a range of 2.0 to 4.0 includes not only the range of 2.0 to 4.0, but also 2.1, 2.3, 3.4, 3.5, and 4.0 individually, as well as any other number subsumed in the range. Furthermore, disclosure of a range of, for example, 2.0 to 4.0 includes the subsets of, for example, 2.1 to 3.5, 2.3 to 3.4, 2.6 to 3.7, and 3.8 to 4.0, as well as any other subset subsumed in the range. Similarly, the disclosure of Markush groups includes the entire group and also any individual members and subgroups subsumed therein. For example, disclosure of the Markush group a hydrogen atom, an alkyl group, an aryl group, or an aralkyl group includes the member alkyl individually; the subgroup alkyl and aryl; and any other individual member and subgroup subsumed therein.

“Alkyl” means an acyclic, branched or unbranched, saturated monovalent hydrocarbon group. Alkyl is exemplified by, but not limited to, methyl, ethyl, propyl (e.g., iso-propyl and/or n-propyl), butyl (e.g., isobutyl, n-butyl, tert-butyl, and/or sec-butyl), pentyl (e.g., isopentyl, neopentyl, and/or tert-pentyl), hexyl, heptyl, octyl, nonyl, and decyl, as well as branched saturated monovalent hydrocarbon groups of 6 or more carbon atoms.

“Alkenyl” means an acyclic, branched or unbranched monovalent hydrocarbon group having a double bond between two carbon atoms. Alkenyl is exemplified by, but not limited to vinyl, allyl, butenyl, pentenyl, and hexenyl, including branched and linear species.

“Aryl” means a cyclic, fully unsaturated, hydrocarbon group. Aryl is exemplified by, but not limited to, cyclopentadienyl, phenyl, anthracenyl, and naphthyl. Monocyclic aryl groups may have 5 to 9 carbon atoms, alternatively 6 to 7 carbon atoms, and alternatively 5 to 6 carbon atoms. Polycyclic aryl groups may have 10 to 17 carbon atoms, alternatively 10 to 14 carbon atoms, and alternatively 12 to 14 carbon atoms.

“Aralkyl” means an alkyl group having a pendant and/or terminal aryl group or an aryl group having a pendant alkyl group. Exemplary aralkyl groups include tolyl, xylyl, benzyl, phenylethyl, phenyl propyl, and phenyl butyl.

“Carbocycle” and “carbocyclic” each mean a hydrocarbon ring. Carbocycles may be monocyclic or alternatively may be fused, bridged, or spiro polycyclic rings. Monocyclic carbocycles may have 3 to 9 carbon atoms, alternatively 4 to 7 carbon atoms, and alternatively 5 to 6 carbon atoms. Polycyclic carbocycles may have 7 to 17 carbon atoms, alternatively 7 to 14 carbon atoms, and alternatively 9 to 10 carbon atoms. Carbocycles may be saturated or partially unsaturated.

“Cycloalkyl” means saturated carbocycle. Monocyclic cycloalkyl groups are exemplified by cyclobutyl, cyclopentyl, and cyclohexyl.

“Halogenated hydrocarbon” means a hydrocarbon where one or more hydrogen atoms bonded to a carbon atom have been formally replaced with a halogen atom. Halogenated hydrocarbon groups include haloalkyl groups, halogenated carbocyclic groups, and haloalkenyl groups. Haloalkyl groups include fluorinated alkyl groups such as trifluoromethyl (CF₃), fluoromethyl, trifluoroethyl, 2-fluoropropyl, 3,3,3-trifluoropropyl, 4,4,4-trifluorobutyl, 4,4,4,3,3-pentafluorobutyl, 5,5,5,4,4,3,3-heptafluoropentyl, 6,6,6,5,5,4,4,3,3-nonafluorohexyl, and 8,8,8,7,7-pentafluorooctyl; and chlorinated alkyl groups such as chloromethyl and 3-chloropropyl. Halogenated carbocyclic groups include fluorinated cycloalkyl groups such as 2,2-difluorocyclopropyl, 2,3-difluorocyclobutyl, 3,4-difluorocyclohexyl, and 3,4-difluoro-5-methylcycloheptyl; and chlorinated cycloalkyl groups such as 2,2-dichlorocyclopropyl, 2,3-dichlorocyclopentyl. Haloalkenyl groups include chloroallyl.

The term “(meth)acrylic acid” as used herein and in the appended claims is intended to serve as a generic expression embracing either or both of acrylic acid and methacrylic acid.

The term “(meth)acrylate” as used herein and in the appended claims is intended to serve as a generic expression embracing either or both of acrylate and methacrylate.

“M-unit” means a siloxane unit having formula R₃SiO_(1/2), where each R independently represents a monovalent atom or organic group. “D-unit” means a siloxane unit having formula R₂SiO_(2/2), where each R independently represents a monovalent atom or group. “T-unit” means a siloxane unit having formula RSiO_(3/2), where each R independently represents a monovalent atom or group. “Q-unit” means a siloxane unit having formula SiO_(4/2). 

1. A polyorganosiloxane hybrid pressure sensitive adhesive composition comprising: (I) a polyorganosiloxane having both aliphatically unsaturated groups and poly(meth)acrylate groups, wherein the polyorganosiloxane comprises unit formula: [R³ _(w)(R⁵—S—R″)(OR₄)_((2-w))Si—O_(1/2)]_(p)[R³ _(v)(R⁵—S—R″)(OR₄)_((1-v))Si—O_(2/2)]_(q)[(R⁵—S—R″)Si—O_(3/2)]_(k)(R⁶R⁷ ₂SiO_(1/2))_(r)(R⁷ ₂SiO_(2/2))_(s)(R⁶R⁷SiO_(2/2))_(t)(R⁷ ₃SiO_(1/2))_(u), where each subscript w is independently 0, 1, or 2, each subscript v is independently 0 or 1, each R³ is an independently selected monovalent hydrocarbon group; each R⁴ is an independently selected alkyl group; each R⁵ is an independently selected divalent hydrocarbon group, each R″ is independently a (meth)acrylate polymer or copolymer, each R⁶ is an independently selected aliphatically unsaturated monovalent hydrocarbon group, each R⁷ is an independently selected monovalent hydrocarbon group free of aliphatic unsaturation, subscript p≥0, subscript q≥0, subscript k≥0, a quantity (p+q+k)≥1, subscript r≥0, subscript s≥0, subscript t≥0, subscript u≥0, a quantity (r+t)≥1, and a quantity (p+q+k+r+s+t+u) is sufficient to provide a molecular weight of at least 50 kDa to the polyorganosiloxane; (II) an organohydrogensilicon compound having, per molecule, at least 3 silicon bonded hydrogen atoms; (III) a hydrosilylation reaction catalyst; optionally (IV) a hydrosilylation reaction inhibitor; (V) a polyorganosilicate resin; and optionally (XX) a solvent.
 2. The composition of claim 1, where in (I) the polyorganosiloxane, R³ has 1 to 18 carbon atoms, R⁴ has 1 to 6 carbon atoms, R⁵ has 1 to 18 carbon atoms, R⁶ has 2 to 18 carbon atoms, and R⁷ has 1 to 18 carbon atoms, R″ has a has a DP of 1 to 1,000; subscript (p+r+u)=2, subscript k=0, a quantity (p+q) is 1 to 100, a quantity (r+t) is 1 to 100, a quantity (p+q+r+s+t+u) is sufficient to provide a molecular weight of 50 kDa to 1,000 kDa to the polyorganosiloxane.
 3. The composition of claim 2, where in (I) the polyorganosiloxane, subscript p is 1 or 2, each R³ is an alkyl group of 1 to 6 carbon atoms, each R⁴ is an alkyl group of 1 to 6 carbon atoms, each R⁵ is an alkylene group of 2 to 8 carbon atoms, R″ has a DP of 5 kDa to 600 kDa, each R⁶ is an alkenyl group selected from vinyl, allyl and hexenyl, and each R⁷ is an alkyl group of 1 to 6 carbon atoms.
 4. The composition of claim 1, where (II) the organohydrogensilicon compound comprises a polyorganohydrogensiloxane of Formula II-1), Formula II-2), and a combination thereof, where Formula II-1) is R¹³ ₃SiO(R¹³ ₂SiO)_(aa)(R¹³HSiO)_(bb)SiR¹³ ₃, and Formula II-2) is R¹³ ₂HSiO(R¹³ ₂SiO)_(cc)(R¹³HSiO)_(dd)SiR¹³ ₂H, where subscript aa has an average value ranging from 0 to 2000, subscript bb has an average value ranging from 2 to 2000, subscript cc has an average value ranging from 0 to 2000, and subscript dd has an average value ranging from 0 to 2000; each R¹³ is independently a monovalent hydrocarbon group.
 5. The composition of claim 4, where the polyorganohydrogensiloxane is selected from the group consisting of: a) dimethylhydrogensiloxy-terminated polydimethylsiloxane, b) dimethylhydrogensiloxy-terminated poly(dimethylsiloxane/methylhydrogensiloxane), c) dimethylhydrogensiloxy-terminated polymethylhydrogensiloxane, d) trimethylsiloxy-terminated poly(dimethylsiloxane/methylhydrogensiloxane), e) trimethylsiloxy-terminated polymethylhydrogensiloxane, and f) a combination thereof.
 6. The composition of claim 1, where (III) the hydrosilylation reaction catalyst comprises a platinum group metal, and the hydrosilylation reaction catalyst is selected from the group consisting of a metal selected from the group consisting of platinum, rhodium, ruthenium, palladium, osmium, and iridium; a compound of the metal; a complex of the compound with low molecular weight organopolysiloxane; and the complex microencapsulated in a resin matrix.
 7. The composition of claim 6, where the hydrosilylation reaction catalyst comprises 1,3-diethenyl-1,1,3,3-tetramethyldisiloxane complexes with platinum.
 8. The composition of claim 1, where (IV) the hydrosilylation reaction inhibitor is present and is selected from the group consisting of an acetylenic alcohol, a cycloalkenylsiloxane, an ene-yne compound, a triazole, a phosphine, a mercaptan, a hydrazine, an amines, a fumarate, a maleate, a nitrile, an ether, carbon monoxide, an alkene, an alcohol, a silylated acetylenic compound, and a combination thereof.
 9. The composition of claim 8, where the hydrosilylation reaction inhibitor comprises an acetylenic alcohol.
 10. The composition of claim 1, where (V) the polyorganosilicate resin comprises unit formula: (R¹⁵ ₂R¹⁶SiO_(1/2))_(x)(R¹⁵ ₃SiO_(1/2))_(y)(SiO_(4/2))_(z), where R¹⁵ is an alkyl group, an aryl group, or an aralkyl group, such as methyl and phenyl; and R¹⁶ is an alkenyl group of 2 to 18 carbon atoms, such as vinyl, allyl or hexenyl; subscript x≥0, subscript y≥0, subscript z>0, a quantity (x+y)>0, and subscripts x, y, and z have values such that 0.9≤(x+y)/z≤1.3.
 11. The composition of claim 10, where subscript x=0, and the polyorganosilicate resin comprises unit formula: (R¹⁵ ₃SiO_(1/2))_(w)(SiO_(4/2))_(z), where subscript w>4.
 12. The composition of claim 1, where the solvent is present, and the solvent is an aromatic hydrocarbon.
 13. The composition of claim 1, where starting material (I) is present in an amount of 15 weight % to 40 weight %; starting material (II) is present in an amount sufficient to provide a molar ratio of SiH content of starting material (II) to aliphatically unsaturated group (R⁶) content of starting material (I) (the SiH:Vi ratio) of 1:1 to 40:1; starting material (III) is present in an amount sufficient to provide 1 ppm to 150 ppm of the platinum group metal; starting material (IV) is present in an amount sufficient to provide a weight ratio of starting material (III):starting material (IV) of up to 40:1; starting material (V) is present in an amount of 5 weight % to 60 weight %; and the solvent is present in an amount of 0 to 70 weight %, wherein all percentages are by weight based on combined weights of all starting materials.
 14. The composition of claim 13, where starting material (I) is present in an amount of 17% to 25%; starting material (II) is present in an amount sufficient to provide the SiH:Vi ratio 10:1 to 35:1; starting material (III) is present in an amount sufficient to provide 2 ppm to 50 ppm, of the platinum group metal; starting material (V) is present in an amount of 25% to 40%; and the solvent is present in an amount of 40% to 60%.
 15. A method for making an adhesive article substrate comprising: optionally i) pre-treating a surface of a substrate, ii) forming a film of the hybrid PSA composition of claim 1 on the surface of the substrate, optionally iii) removing all or a portion of the solvent, and iv) curing the hybrid PSA composition to form a hybrid PSA.
 16. The composition of claim 1, where in (I) the polyorganosiloxane, R″ comprises (meth)acrylate monomer units selected from the group consisting of acrylic acid, butyl acrylate, butyl methacrylate, 2-ethylhexylacrylate, 2-ethylhexylmethacrylate, isobutyl acrylate, isobutyl methacrylate, methyl methacrylate, methacrylic acid, benzyl methacrylate, phenyl methacrylate, and a combination thereof.
 17. The composition of claim 16, where the (meth)acrylate monomer units are selected from the group consisting of acrylic acid, butyl acrylate, butyl methacrylate, 2-ethylhexylacrylate, methyl methacrylate, and a combination thereof.
 18. The composition of claim 3, where in (I) the polyorganosiloxane, each R³ is methyl, each R⁴ is methyl or ethyl, each R⁵ is methyl, propyl, or undecyl, R″ has a DP of 5 kDa to 600 kDa, each R⁶ is vinyl, and each R⁷ is methyl. 